Microstructure and properties of in-situ composite coatings prepared by plasma spraying MoO3–Al composite powders

Yan-wei Wang,Xing-yu Wang,Xiao-long Wang,Yong Yang,Yu-hang Cui,Yu-duo Ma,Wen-wei Sun
DOI: https://doi.org/10.1016/j.ceramint.2020.08.227
IF: 5.532
2021-01-01
Ceramics International
Abstract:<p>MoO<sub>3</sub>–Al composite powders were used for preparing in situ composite coatings. Effects of the composition of MoO<sub>3</sub>–Al composite powder on the microstructure and properties of the as-prepared coatings were investigated. The results show that the main phases of the as-prepared coatings were γ-Al<sub>2</sub>O<sub>3</sub> and Mo. An optimal composition (63 wt%) of MoO<sub>3</sub> in MoO<sub>3</sub>–Al composite powder was demonstrated. The porosity of the as-prepared composite coatings decreased first and then increased with the increase of MoO<sub>3</sub>. This is attributed to the fact that the melting state of the powder during plasma spraying is closely involved in the content of MoO<sub>3</sub>. The coating prepared by composite powder with 63 wt% MoO<sub>3</sub> had the most Al<sub>2</sub>O<sub>3</sub> and the highest microhardness. The wear resistance of 63 wt% MoO<sub>3</sub> composite coating was the best among four coatings with different content of MoO<sub>3</sub>, which is attributed to its high hardness and good toughness.</p>
materials science, ceramics
What problem does this paper attempt to address?