Structure and Properties of Isosorbide type Polycarbonate/ABS Blend

SH Wang,W Zhang,S Haruo,ZX Guo,J Yu

DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16364

2017-01-01

Acta Polymerica Sinica

Abstract:Blending type of ABS with different polybutadiene rubber (PB) and polyacrylonitrile (AN) contents in SAN phase is prepared at 240 degrees C to study the effects of PB and AN content on the structure and the properties of DB/ABS blends. Different kinds of productive ABS along with the blend-type ABS are used to compare the properties of PC/ABS and DB/ABS blends comprehensively. All blends are made by melt blending for 10 min with sheer rate of 30 r/min. The result shows that, in DB/Blend-type ABS (70/30) blends, PB content exhibits significant influence on the tensile properties. Samples with 6.3 wt% of PB always show the best performance both in yield strength and elongation at break when AN content is fixed at 18 wt%, 25 wt% and 30 wt%; while increasing AN content in the sample with the same PB content would result in better blends properties even not so obvious as PB content. Scanning electron microscopy gives exactly the same trend for phase morphology with PB and AN contents, revealing best uniform scale of dispersed phase (ABS) among 0.5 - 1.2 mu m at 6.3 wt% of PB. Thermal gravimetric analysis shows that all DB/ABS blends have good thermal stability, which is not obviously affected by PB content and AN content. Single peak of glass transition shows good compatibility in the DB/ABS blends. Excellent compatibility of DB with ABS in the sample is exhibited through dynamic mechanical analysis. The glasstransition temperature of DB/ABS blends are closed to that of DB, mildly affected by PB and AN content. Besides, both blending type ABS and different kinds of productive type ABS are used to compare the properties of DB/ABS blends and traditional bisphenol-A-type PC/ABS blends. Basic laws of tensile properties in DB/ABS remain the same as in PC/ABS blends using different types of ABS.