Mechanical and Morphological Properties and Deformation Mechanisms of Acrylonitrile-Butadiene-Styrene/Poly(ϵ-Caprolactone) Blends with Varied Matrix Composition

Haihe Song,Shulin Sun,Huixuan Zhang

DOI: https://doi.org/10.1080/00222348.2013.860302

2014-01-01

Abstract:Acrylonitrile-butadiene-styrene and poly(e-caprolactone) blends (ABS/PCL) were prepared by mixing styrene-co-acrylonitrile (SAN), polybutadiene-g-SAN (PB-g-SAN), and PCL with varied SAN and PCL composition. PCL is miscible with SAN and can improve the matrix toughness. The impact strength and elongation at break of the ABS/PCL blends increased with the PCL content. When the PCL content was lower than 20 wt%, the improvement of impact strength for the blends was not obvious. A significant increase of impact strength took place when the PCL content was between 20 and 25 wt%. When PCL content was more than 20 wt%, the impact strength was higher than 800 J/m which shows the super toughness. The addition of PCL improved the dispersed phase morphology of PB-g-SAN in the matrix and the interfacial adhesion increased. Deformation observations showed that, when the PCL content was lower than 20 wt%, crazing was the major deformation mode. When the PCL content was 20 wt%, crazing and slight shear yielding could be found. When the PCL content was more than 20 wt%, cavitation of rubber particles and shear yielding of the matrix were the major deformation modes. The cause of the change of the deformation mode lies in the varied matrix composition which modifies the crazing and yielding stresses of the matrix and the final fracture mode and impact toughness.