Abstract:Glycidyl methacrylate functionalized acrylonitrile-butadiene-styrene (ABS-g-GMA) particles were prepared and used to toughen polylactide (PLA). The characteristic absorption at 1728 cm(-1) of the Fourier transform infrared spectra indicated that glycidyl methacrylate (GMA) was grafted onto the polybutadiene phase of acrylonitrile-butadiene-styrene (ABS). Chemical reactions analysis indicated that compatibilization and crosslinking reactions took place simultaneously between the epoxy groups of ABS-g-GMA and the end carboxyl or hydroxyl groups of PLA and that the increase of GMA content improved the reaction degree. Scanning electron microscopy results showed that 1 wt % GMA was sufficient to satisfy the compatibilization and that ABS-g-GMA particles with 1 wt % GMA dispersed in PLA uniformly. A further increase of GMA content induced the agglomeration of ABS-g-GMA particles because of crosslinking reactions. Dynamic mechanical analysis testing showed that the miscibility between PLA and ABS improved with the introduction of GMA onto ABS particles because of compatibilization reactions. The storage modulus decreased for the PLA blends with increasing GMA content. The decrease in the storage modulus was due to the chemical reactions in the PLA/ABS-g-GMA blends, which improved the viscosity and decreased the crystallization of PLA. A notched impact strength of 540 J/m was achieved for the PLA/ABS-g-GMA blend with 1 wt % GMA, which was 27 times than the impact strength of pure PLA, and a further increase in the GMA content in the ABS-g-GMA particles was not beneficial to the toughness improvement. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 122:2992-2999, 2011

Investigation of the Properties of PBT/ABS-g-GMA Blends Modified with Epoxy Resin of Mid-Molecular Weights

Influence of Epoxy Resin on the Morphological and Rheological Properties of PBT/ABS Blends Compatibilized by ASMA

Toughening of Poly(butylene Terephthalate) with Epoxy-Functionalized Acrylonitrile–butadiene–styrene

Investigation of the Properties of Epoxy-Functionalized Acrylonitrile-butadiene-styrene Toughened Poly (butylene Terephthalate) and Its Blends

Properties of Poly(butylene Terephthalate)/bisphenol A Polycarbonate Blends Toughening with Epoxy-Functionalized Acrylonitrile–Butadiene–Styrene Particles

ABS-g-GMA Toughened Poly (butylene terephthalate)

Research on effect of ABS,MAH,DCP on property of PA6/ABS blend

Thermal and Mechanical Properties of Poly(butylene Terephthalate)/epoxy Blends

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Effect of Abs Grafting Degree and Compatibilization on the Properties of Pbt/Abs Blends

Toughening of Pbt/Pc Blends with Epoxy Functionalized Core-Shell Modifiers

Effect of Epoxy-Functionalised Core-Shell Particles on Properties of Poly(Butylenes Terephthalate) (Pbt)

Influence of the Degree of Grafting on the Morphology and Mechanical Properties of Blends of Poly(butylene Terephthalate) and Glycidyl Methacrylate Grafted Poly(ethylene‐co‐propylene) (EPR)

Influence of Methyl Methacrylate-Co-glycidyl Methacrylate Copolymers on the Compatibility, Morphology and Mechanical Properties of Poly(butylene Terephthalate) and Polycarbonate Blends

Toughening of PBT by POE/POE-g-GMA Elastomer Through Regulating Interfacial Adhesion and Toughening Mechanism

Rheology of Poly(lactic Acid)/poly(trimethylene Terephthalate) Blends Compatibilized by Clay or Maleic Anhydride-Grafted Poly(ethylene-Octene) Elastomer

Influence of Core-Shell Particles Structure on the Morphology and Brittle-Ductile Transition of Pbt/Abs-G-Gma Blends

Polylactide Toughening with Epoxy‐functionalized Grafted Acrylonitrile–butadiene–styrene Particles

Toughening of Polylactide with Epoxy-Functionalized Methyl Methacrylate-Butadiene Copolymer

Blending ABS resin and its effect on structure and properties of PC/ABS BLEND alloy

Toughening of PBT/PC Blends with Core-Shell Modifier