Abstract:A detailed microstructural study of ATI 718Plus superalloy produced by the wire-arc additive manufacturing (WAAM) process was performed through the use of scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron probe micro-analysis (EPMA), and electron backscatter diffraction (EBSD). Extensive formation of eutectic solidification microconstituents including Laves and MC-type carbide phases, induced by micro-segregation, are observed in the build of the alloy in the as-deposited condition. Notwithstanding the significant segregation of niobium (Nb), which has been reported to promote the formation of the δ-phase in ATI 718Plus, only η-phase particles are observed in the deposit. Excessive precipitation of η-phase particles is found to be linked to Laves phase particles that are partially dissolved in the deposit after post-deposition heat treatment (PDHT). The EBSD analysis shows a high textured build in the 〈100〉 directions with only a few misoriented grains at the substrate–deposit boundary and the top of the deposit. Investigation on the hardness of the build of the alloy, in the as-deposited condition, showed a softened zone about 2 mm wide at the deposited metal heat affected zone (DMHAZ), which has not been previously reported and potentially damaging to the mechanical properties. An extensive analysis with the use of both microstructural characterization tools and theoretical calculations shows that the DMHAZ has the lowest volume fraction of strengthening precipitates (γ′ and γ″) in terms of their number density, which therefore induces the observed softness. Delayed re-precipitation kinetics and the extent of the precipitation of γ′ and γ″ in the DMHAZ which is related to the diffusion of segregated solute elements from the interdendritic regions are attributed to this phenomenon. The microstructural analyses discussed in this work are vital to adequate understanding of properties of ATI 718Plus produced by the additive manufacturing process technique.

Research Progress of Alloy ATI 718Plus in China

Effect of the precipitation of the η-Ni3Al0.5Nb0.5 phase on the microstructure and mechanical properties of ATI 718Plus

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

The Effect of Phosphorus on the Microstructure and Mechanical Properties of ATI 718plus Alloy

Enhancing tensile properties of wrought Ni-based superalloy ATI 718Plus at elevated temperature via morphology control of η phase

Microstructure Evolution of Inconel 718 Superalloy During Hot Working and Its Recent Development Tendency

Microstructural Analyses of ATI 718Plus® Produced by Wire-ARC Additive Manufacturing Process

Mechanically Blended Al: Simple but Effective Approach to Improving Mechanical Property and Thermal Stability of Selective Laser-Melted Inconel 718

Evaluation on Elevated-Temperature Stability of Modified 718-Type Alloys with Varied Phase Configurations

Insight into Elongation and Strength Enhancement of Heat-Treated LPBF Ni-based Superalloy 718 Using In-Situ SEM-EBSD

Microstructural evolution and mechanical properties of IN718 alloy fabricated by selective laser melting following different heat treatments

Microstructure evolution and mechanical properties of a nickel-based superalloy repaired using wire and arc additive manufacturing

Research Progress of Wrought Superalloys in China

Novel in situ synthesized carbide reinforced Ni base composite for structural castings with high creep resistance

Improving High-Temperature Mechanical Properties of Additively Manufactured Inconel 718 Through Heat Treatment

Microstructure and Mechanical Properties of a New Ni-Cr-Fe-W-Al Alloy for Advanced Ultra-Supercritical Power Plants

Solidification behavior of Pt-containing 718Plus superalloy

Strengthening Effects and Thermal Stability of the Ultrafine Grained Microstructure of a Nickel Base Superalloy at Room and Elevated Temperatures

Precipitation behaviors of the rapidly-solidified Allvac 718Plus superalloy during aging treatment

A thermochemical database from high-throughput first-principles calculations and its application to analyzing phase evolution in AM-fabricated IN718

Microstructures and High-Temperature Mechanical Properties of Inconel 718 Superalloy Fabricated via Laser Powder Bed Fusion