Insight into Elongation and Strength Enhancement of Heat-Treated LPBF Ni-based Superalloy 718 Using In-Situ SEM-EBSD

Muhammad Rizwan,Rafi Ullah,Junxia Lu,Jin Wang,Yuefei Zhang,Ze Zhang

DOI: https://doi.org/10.1016/j.msea.2024.147163

2024-01-01

Abstract:This study presents a detailed investigation into the deformation behaviour and the factors affecting the strength and ductility of laser powder bed fusion (LPBF) Ni-based superalloy 718 (Inconel 718) in both as-printed and heat-treated conditions using in-situ SEM + EBSD. The results show that following post-deposition high homogenization temperatures, the columnar grain structure of the as-printed Inconel 718 alloy successfully transformed to a nearly uniform grain size and the subsequent aging processes facilitated the precipitation of strengthening phases (gamma ', ' , gamma"). The specimen subjected to heat treatment (HT1) exhibited higher strength but lower ductility, while the as-printed specimen shows higher tensile elongation due to high initial dislocation density. In contrast, the heat-treated (HT2) specimen presented a more optimal combination of strength and ductility. The underlying mechanism for the enhanced tensile properties in the HT2 specimen was nearly homogeneous deformation trend across the grains and ultrafine precipitation of hardening phases. In addition, the twin boundaries were stable in the early deformation stages and maintained their orientation. Multiple slip systems were activated at the high-deformation stage, resulting in a high proportion of geometric necessary dislocations. Further, the interaction of deformation-induced dislocation with twin boundaries transformed them into general boundaries such as high and low-angle grain boundaries, ultimately increasing ductility. On contrary, in the HT1 specimen, the deformation inhomogeneity in grains enabled the strain localization at grain boundaries, which ultimately caused the early formation of cracks.