Abstract:2.5-D braided high-alumina fabric-reinforced silica matrix composite materials are being developed as functional structural composites with thermal load-bearing capacity for the top thin face sheet of an integrated thermal protection system (TPS). This study seeks to elucidate the mechanical behavior of a 2.5-D braided top face sheet composite material subjected to off-axis compression, while the sandwich TPS is under deflection caused by the bending moment resulting from the temperature gradient in the thickness direction and the aerodynamic pressure on the top face sheet panel. The effective compressive modulus and ultimate strength along the warp direction are significantly lower than those along the weft direction. Both decrease as the off-axis loading angle increases, indicating anisotropy. A nonlinear compressive stress–strain response with extensive damage along the warp yarn direction, while the weft yarn direction exhibits a quasi-linear response with minor damage before fracture. Within the framework of continuum damage mechanics, fiber kinking and transverse inter-fiber cracking of fiber bundles with the linear damage evolution law are all considered simultaneously for the progressive damage model. To account for the interaction between multiple damage mechanisms in the fiber yarn, a joint degradation induced by multiple damage mechanisms is first proposed. The analysis reveals that the anisotropy of failure under compression is primarily due to the warp fiber bundle's much larger undulation than the weft fiber bundle, which causes severe bending-dominated damage. Using the calibrated model, the qualitative effects of material thickness and yarn geometry size on the compressive mechanical properties of materials are analyzed.

Fracture Failure Analysis and Bias Tearing Strength Criterion for PVDF Coated Biaxial Warp Knitted Fabrics

Mechanical properties analysis of architectural PVDF/PES fabrics with uni-tensile and bi-axial test

Experimental studies on tear failure of PVC coated fabric

Off-axis tearing properties of the biaxial warp-knitted fabrics

Multiaxial failure mechanism of 3D triple-twill warp-lining woven composites

Anisotropic failure analysis of 2.5-D braided composites under compression

Experimental investigation on mechanical response and failure analysis of 3D multi-axial warp knitted hybrid composites

Tensile properties of multilayered biaxial weft knitted fabric reinforced composite material

Central tearing behavior of PVDF coated fabrics with multiple initial notches

Exploring in-plane shear characteristics of multilayer biaxial weft knitted fabrics through a micro-scale virtual fiber modeling

Mechanical Responses and Damage Morphology of Laminated Fabrics with a Central Slit under Uniaxial Tension: A Comparison Between Analytical and Experimental Results

Experimental Study on the Mechanical Behavior and Failure Mechanism of 3d MWK Carbon/epoxy Composites under Quasi-Static Loading

Flexural Failure Mechanisms of Three-Dimensional Woven Textile Sandwich Panels: Experiments

Effect of triaxial woven fabric on bending properties of unidirectional composites

Progressive damage modelling and experimental investigation of three-dimensional orthogonal woven composites with tilted binder

Off-axial Angle Sensitivity of 3D Orthogonal Woven Composite Failure Behavior Subjected to In-Plane Compressive Loading

Directionally Oriented Reinforcements of Warp-Knitted Fabrics for Composite Preforms

Experimental Investigations on the Failures of Woven Textile Sandwich Panels

Analysis of in-plane compression failure mechanism in carbon fiber braided composite with different off-axial angles

Mechanical behavior of PVDF membrane based on the uni-/bi-axial loading experiments

Sheet forming of the multi-layered biaxial weft knitted fabric reinforcement. Part I: On hemispherical surfaces