Abstract:<p>3D multi-axial warp knitted (MWK) hybrid composites were fabricated successfully. Tensile, compression, bending and shear properties at high temperatures, and impact tests were performed to reveal mechanical response and failure mechanism. The results show the composites exhibit linear feature and brittle, except from shear curve which shows distinct nonlinear behavior. Meanwhile, the curves show non-linear, long plasticity plateau and failure feature in steps at high temperatures. In addition, tension failure is 0° fibers breakage and pulling out, and 90° fibers tearing; Out-of-plane compression behaves as 45° shear fracture and delaminating; while in-plane compression shows delaminating; Bending failure is tearing of fibers and interface debonding on compression surface, 0° fibers fracture on tension surface and fiber layers delaminating; Shear failure exhibits growing matrix shear damage and debonding, 90° fibers fracture in shear, and 0° fibers' compression; Impact failure shows "star-shaped" mode under quasi-static and "pyramid -shaped" mode with increasing impact velocity. With increasing the temperature, the materials become soft and plastic. The matrix yielding and cracking, interface debonding, and fiber layers delaminating feature become prominent.</p>
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the mechanical response and failure analysis of 3D multi - axial warp - knitted hybrid composites at high temperatures. Specifically, the researchers prepared 3D multi - axial warp - knitted Kevlar/glass hybrid composites, and through tensile, compressive, bending and shear property tests as well as impact tests, they explored the mechanical properties and failure mechanisms of these materials under different temperature conditions. The main purpose of the study is to establish a performance database for 3D multi - axial warp - knitted hybrid composites, providing a basis for their potential applications.
The following points are discussed in detail in the paper:
1. **Tensile properties and failure mechanisms at high temperatures**:
- The tensile stress - strain curves of the composites at different temperatures were studied, and it was found that as the temperature increased, the tensile strength and modulus of the composites decreased significantly.
- The tensile failure modes at different temperatures were analyzed, including 0° fiber breakage, 90° fiber tearing, and interface debonding, etc.
2. **Compressive properties and failure mechanisms at high temperatures**:
- The in - plane and out - of - plane compressive properties of the composites at different temperatures were studied, and it was found that as the temperature increased, the compressive strength and modulus gradually decreased.
- The compressive failure modes at different temperatures were analyzed, including 45° shear fracture, delamination, and interface debonding, etc.
3. **Bending properties and failure mechanisms at high temperatures**:
- The bending properties of the composites at different temperatures were studied, and it was found that as the temperature increased, the bending strength and modulus decreased significantly.
- The bending failure modes at different temperatures were analyzed, including local damage on the compression surface, 0° fiber bending deformation, 90° fiber tearing, and interface debonding, etc.
4. **Shear properties and failure mechanisms at high temperatures**:
- The shear properties of the composites at different temperatures were studied, and it was found that as the temperature increased, the shear strength and modulus gradually decreased.
- The shear failure modes at different temperatures were analyzed, including 0° fiber buckling and shear fracture, 90° fiber tearing along the weak interface, and delamination, etc.
Through these studies, the authors hope to provide important reference data and theoretical support for the applications of 3D multi - axial warp - knitted hybrid composites in aerospace, marine, and construction fields, etc.