Experimental study on the fabrication, high-temperature properties and failure analysis of 3D seven-directional braided composites under compression

Dian-sen Li,Ying Yang,Lei Jiang

DOI: https://doi.org/10.1016/j.compstruct.2021.113934

IF: 6.3

2021-07-01

Composite Structures

Abstract:<p>Three-dimensional seven-directional (3D7d) braided composites had potential application in aerospace field and they were successfully fabricated. The compression mechanical properties of composites are thoroughly studied based on different load modes and high temperature influence. Then, the failure mechanism is evaluated using Macro-fracture and SEM micrographs. The results show that as temperature increases, the stress vs. strain curves decrease monotonically and present nonlinearity feature. Meanwhile, the out-of-plane compression properties among three loading direction modes is the best, following by longitudinal, and transverse is the worst. 3D7d structure significantly improves the out-of-plane properties compared to 3D6d, 3D5d and 3D4d structure. Meanwhile, it also makes the transverse properties higher than those of 3D5d and 3D4d structure. Moreover, failure mechanism of 3D7d braided composites varies with loading mode and temperature. Out-of-plane compression shows multiple 45° shear failure, and compacted gradually. Longitudinal compression behaves as local outward expansion and multiple shear features along the braiding yarn/matrix interface. Transverse compression exhibits shear fracture at 45° in-plane direction. At high temperatures, the shear fracture feature still dominated the main failure. The matrix gets soft, cracks and comes plastic, and the interfacial adhesion of fiber/matrix is significantly reduced.</p>

mechanics,materials science, composites

What problem does this paper attempt to address?

This paper aims to explore the mechanical properties and failure mechanisms of three - dimensional seven - directional (3D7d) braided composites under high - temperature conditions. Specifically, the research objectives include:

1. **High - temperature compression properties**: Through experiments under different loading modes (out - of - plane, longitudinal and transverse compression) and different temperature conditions, evaluate the compressive mechanical properties of 3D7d braided composites. The study found that as the temperature increases, the stress - strain curve shows a monotonically decreasing trend and exhibits non - linear characteristics.

2. **Failure mechanisms**: Use macroscopic fractures and scanning electron microscope (SEM) microscopic images to analyze the failure mechanisms of 3D7d braided composites under different loading modes and temperature conditions. The research results show that:
- **Out - of - plane compression**: It is mainly characterized by 45° shear failure and gradually compacts.
- **Longitudinal compression**: It is characterized by local outward expansion and multiple shear features along the braided yarn/matrix interface.
- **Transverse compression**: It is characterized by shear fracture in the 45° plane direction.

3. **Structure comparison**: Compared with 3D6d, 3D5d and 3D4d structures, the 3D7d structure significantly improves the out - of - plane performance and makes the transverse performance better than that of 3D5d and 3D4d structures.

4. **Temperature influence**: The influence of temperature on the compressive properties of 3D7d braided composites was studied. The results show that as the temperature increases, the out - of - plane, longitudinal and transverse compressive properties all decrease, among which the out - of - plane compressive property decreases most obviously.

5. **Loading direction influence**: The influence of different loading directions (out - of - plane, longitudinal and transverse) on the high - temperature properties of 3D7d braided composites was studied. The results show that the out - of - plane compressive property is the best, followed by the longitudinal, and the transverse is the worst.

6. **Braiding structure influence**: The influence of the braiding structure on the high - temperature properties of 3D7d braided composites was studied. Compared with 3D6d, 3D5d and 3D4d structures, the 3D7d structure has the highest strength and modulus in the out - of - plane direction, but is slightly inferior in the longitudinal and transverse directions.

In conclusion, through systematic experimental research, this paper reveals the compressive properties and failure mechanisms of 3D7d braided composites under high - temperature conditions, providing important data support and theoretical basis for the application of this material in the aerospace field.