Abstract:The feasibility of a facile technological route to preparation of refractory materials from a ferronickel slag with the addition of sintered magnesia was verified in this study based on the thermodynamics analysis and the experimental exploration of the effect of the sintered magnesia addition on the phase transformation of ferronickel slag during the sintering process. For the first time, the results of thermodynamics calculation, X-ray diffraction (XRD), and scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDS) analyses revealed that the original phase of the slag can be transformed to high melting point phases by addition of MgO during the sintering process at high temperatures (e.g., 1350 degrees C). Specifically, the olivine in ferronickel slag decomposed initially, generating a low-iron olivine phase and an enstatite phase. With increasing addition of sintered magnesia, the enstatite phase changed to forsterite, and the iron, aluminum, and chromium components in the ferronickel slag converted to high melting point spinel phases, including magnesium aluminate spinel and magnesium chromate spinel via a low-magnesium transient phase. The experimental results showed that a good refractory material with refractoriness of 1660 degrees C, bulk density of 2.92 g/cm(3), apparent porosity of 1.82%, and compressive strength of 100.61 MPa could be obtained when the slag was sintered with addition of 20 wt % sintered magnesia at 1350 degrees C for 3 h. Due to the low production cost and property superiority of the prepared refractory material over commercial counterparts, the method proposed in this study is expected to have widespread applications in recycling of ferronickel slag.

Promoting Spinel Formation and Growth for Preparation of Refractory Materials from Ferronickel Slag

Valorization of Ferronickel Slag into Refractory Materials: Effect of Sintering Temperature

Preparation of Refractory Materials by Co-sintering of Ferronickel Slag and Ferrochromium Slag: Thermodynamic Analysis

Preparation of Refractory Materials from Ferronickel Slag

Facile Route for Preparing Refractory Materials from Ferronickel Slag with Addition of Magnesia

Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

Synergistic preparation of forsterite‐spinel refractory materials from ferronickel slag and ferrochromium slag

Chromium: A Double-Edged Sword in Preparation of Refractory Materials from Ferronickel Slag

Assessing Magnesia Effect on Preparing Refractory Materials from Ferrochromium Slag

From ferronickel slag to value-added refractory materials: A microwave sintering strategy

Thermodynamic Characteristics of Ferronickel Slag Sintered in the Presence of Magnesia

Preparation of Refractory Materials from Electric Furnace Ferronickel Slag and Blast Furnace Ferronickel Slag: A Comparison

Alumina-enhanced Valorization of Ferronickel Slag into Refractory Materials under Microwave Irradiation

Preparation of Magnesium Aluminum Ferrite Spinel by Microwave Sintering

Mechanism of in-situ formation of spinel and its effect on the mechanical properties of Al2O3–C refractories

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite

Effects of Sintering Temperature and Time on Preparation of Refractory Materials from Ferronickel Slag Under Microwave Irradiation

Strengthening Sintering Of Limonitic Nickel Laterite By Substituting Ferronickel Tailings For Sintering Fluxes

Effect of Magnesia-Alumina Spinel Precursor Sol on the Sintering Property of Fused Magnesia Refractory

Tailoring Tactics for Preparation of Superior Thermal Insulation Materials from Blast Furnace Ferronickel Slag: Control of Sintering Temperature

Thermodynamic calculation and microstructure characterization of spinel formation in MgO–Al2O3–C refractories