Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

Novel Colloidal Silica Technology For In Situ Spinelization in MgO-Containing Refractories

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Mechanism of in-situ formation of spinel and its effect on the mechanical properties of Al2O3–C refractories

The microstructure evolution and performance enhancement of MgO-C refractories by the addition of MA90 spinel micro-powder

Study on Fabrication of Al2O3-MgO (Spinel)-Sialon Composite Refractory

Thermodynamic calculation and microstructure characterization of spinel formation in MgO–Al2O3–C refractories

Effects of Sm2O3 addition on sintering behavior of pre-synthesized magnesia-rich magnesium aluminate spinel

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite

M- S-H formation in MgO-SiO2slurries via wet milling for magnesia based castables

A strategy for controlling microstructure and mechanical properties of microporous spinel (MgAl2O4) aggregates from magnesite and Al(OH)3

Development of an Ultra-Low Carbon MgO Refractory Doped with α-Al2O3 Nanoparticles for the Steelmaking Industry: A Microstructural and Thermo-Mechanical Study

Microstructural and Optical Properties of MgAl2O4 Spinel: Effects of Mechanical Activation, Y2O3 and Graphene Additions

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

Microstructures and Strengths of Microporous MgO‐Al2O3 Refractory Aggregates Using Two Types of Magnesite

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

Novel Synthesis of High Surface Area MgAl2O4 Spinel As Catalyst Support

Gelcasting of Alumina-Spinel Refractories

Effect of Magnesia-Alumina Spinel Precursor Sol on the Sintering Property of Fused Magnesia Refractory

A novel low thermal conductivity refractory aggregate for high-temperature applications: Lightweight microporous alumina-rich spinel (Mg0.4Al2.4O4)

Preparation and Characterization of Corundum-Mullite-Spinel Refractories from Low-Grade Bauxite and Magnesite Ores

In Situ Synthesis and Interfacial Bonding Mechanism of SiC in MgO–SiC–C Refractories