Enhancing mechanism of improved slag resistance of Al2O3-spinel castables added with pre-synthesized (Al,Cr)2O3 micro-powder
Xinxin Li,Jing Li,Ling Zhang
DOI: https://doi.org/10.1016/j.ceramint.2021.08.235
IF: 5.532
2021-12-01
Ceramics International
Abstract:In order to enhance the slag resistance of Al2O3-spinel castables, (Al,Cr)2O3 is added into Al2O3-spinel system as a pre-synthesized micro-powder. Firstly, (Al,Cr)2O3 micro-powder is synthesized by sintering under reduction conditions to prevent the formation of hexavalent chromium. The Al2O3-spinel castables are prepared using tabular alumina, fused spinel, α-Al2O3 micro-powder, calcium aluminate cement and (Al,Cr)2O3 micro-powder as the raw materials. The bulk density, porosity, mechanical properties, and slag resistance of the samples are tested. Afterward, the effects of (Al,Cr)2O3 micro-powder (0–3 wt%) on the slag resistance and microstructures of the Al2O3-spinel castables are assessed by X-ray diffraction (XRD) and energy-dispersive (SEM-EDS) analysis. The results show that the addition of (Al,Cr)2O3 micro-powder can could inhibit the deteriorating effects of Cr3+ on the mechanical properties of the samples. The microstructure results also shows that with the addition of the (Al,Cr)2O3 micro-powder, a secondary solid solution of Ca(Al,Cr)12O19 formed, causing the unit cell to become larger. In the slag erosion area, CA6 crystals formed with network-like interwoven structures, high density, and greater thickness. These characteristics significantly reduce the erosion and permeability indices of the castables, and improve the slag erosion resistance of the material.
materials science, ceramics