Enhanced thermal shock resistance of hydratable magnesium carboxylate bonded castables via in-situ formation of micro-sized spinel

Guoqing Xiao,Jianjun Chen,Donghai Ding,Changkun Lei,Yunfei Zang,Xiaochuan Chong,Jiyuan Luo,Jiaoyang Qu

DOI: https://doi.org/10.1016/j.ceramint.2021.07.110

IF: 5.532

2021-10-01

Ceramics International

Abstract:Our previous investigations indicate that the thermal shock resistance (TSR) of hydratable magnesium carboxylate (HMC) bonded Al2O3–MgO castables is superior to castables bonded with calcium aluminate cement as a result of the in-situ formation of micro-sized spinel (MgAl2O4). In the present study, to further enhance the TSR of HMC bonded castables, the submicron alumina powders were added into the castables to decrease the size of the spinel particle through a reaction of submicron alumina with nano magnesia pyrolyzed from HMC. The effects of submicron alumina powders on the TSR, slag corrosion resistance, and microstructure of HMC bonded castables were investigated. The results show that the size of the in-situ spinel particle decreases from approximately 2 μm to approximately 0.8 μm and the spinel gradually transforms into the aluminum-rich spinel after adding submicron alumina powders. The residual strength retention ratio of the samples raises from 37.5% to 50.0%, and the thermal stress damage resistance index (R՛՛՛՛) of the samples increases from 3.1 m to 7.2 m with the increase in the amount of submicron alumina to 2.0 wt% after thermal shock. The microcracks in the castables matrix of sample 2A are more and shorter than those of sample 0A after thermal shock. This is attributed to the fact that the resistance of microcracks propagation in the castables is enhanced via smaller spinel with uniform distribution. Besides, the penetration index of the castables decreases from 20.8% to 9.8% with the increase of submicron alumina content powders to 2.0 wt%. This is because the submicron alumina powders decrease the porosity of the castables, and the smaller size of the aluminum-rich spinel has a stronger adsorption capacity for Fe2+ ions.

materials science, ceramics