Abstract:Magnesium aluminate spinel (MgAl2O4) ceramics are high-performance and carbon-free materials widely used in both military and civilian fields. However, it is usually challenging to densify during the solid-state sintering process. The excellent properties of some rare earth oxides have been proved to promote the densification of MgAl2O4 spinel ceramics. But the mechanism of promoting sintering is not clear. In the present work, MgAl2O4 spinel ceramics have been successfully fabricated by co-doping CeO2 and La2O3 via a single-stage solid-state reaction sintering. The effects of addition amounts of CeO2 and La2O3 on phase compositions, microstructures, sintering characteristics, cold compressive strength, and thermal shock resistance of as-prepared MgAl2O4 spinel ceramics were systematically investigated. The results show that by co-doping CeO2 and La2O3 can increase the defect concentration due to the lattice distortion. This could promote the movement of Al3+ and Mg2+ at high temperature, which is beneficial to the formation of more secondary MgAl2O4 spinel. t-ZrO2 with more Ce4+ filling between spinel grains could prevent the growth of grains and promote the densification, besides the new-formed LaAlO3 that was mainly distributed along the grain boundary of the MgAl2O4 phase, both of which were favorable for the formation of dense microstructure of MgAl2O4 spinel materials. At the same time, the formation of more secondary MgAl2O4 spinel and sintering densification also improve the mechanical properties of spinel ceramics. La3+ will segregate to the spinel grain boundary, preventing grain boundary movement and absorbing the main crack's fracture energy. With 3 wt% CeO2 and 3 wt% La2O3 co-doping, the bulk density of the sample increased from 3.02 g∙cm−3 to 3.55 g∙cm−3; the apparent porosity decreased from 12.21% to 9.97%; the cold compressive strength increased from 172.88 MPa to 189.54 MPa; and the residual strength retention ratio after thermal shock increased from 84.92% to 89.15%.

Enhancement of thermal shock resistance of Al2O3–MgAl2O4 composites by controlling the content and distribution of spinel phase

Enhanced thermal shock resistance of hydratable magnesium carboxylate bonded castables via in-situ formation of micro-sized spinel

Effect of Molar Ratios of MgO/Al2O3 on the Sintering Behavior and Thermal Shock Resistance of MgOAl2O3SiO2 Composite Ceramics

Enhanced thermal shock resistance of ZrO2-reinforced Al2O3–CaAl12O19 composites prepared from ferrotitanium slag: Crack propagation resistance mechanisms

Effect of Al2O3 on Sintering and Thermal Shock Resistance of MgO Ceramic

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

Effect of Al2O3 + 4sio2 Additives on Sintering Behavior and Thermal Shock Resistance of MgO-Based Ceramics

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

Effect of AlO + 4SiO Additives on Sintering Behavior and Thermal Shock Resistance of MgO-Based Ceramics

Investigation on mechanical and thermal properties of MgAl2O4-Mg2TiO4 solid solutions with spinel-type structure

Sintering behavior and thermal shock resistance of aluminum titanate (Al2TiO5)-toughened MgO-based ceramics

Improved thermal shock resistance of low-carbon Al2O3–C refractories fabricated with C/MgAl2O4 composite powders

A strategy for controlling microstructure and mechanical properties of microporous spinel (MgAl2O4) aggregates from magnesite and Al(OH)3

Enhanced performance of low-carbon MgO–C refractories with nano-sized ZrO2–Al2O3 composite powder

Effect of MgO addition on properties of reaction-sintered ZrO2-toughened Al2O3 multiphase ceramic

Mechanism of in-situ formation of spinel and its effect on the mechanical properties of Al2O3–C refractories

The effect of MnO2 additive on the microstructure and mechanical properties of magnesium aluminate spinel

Enhanced thermal shock response of Al 2 O 3 –graphite composites through a layered architectural design

Preparation and properties of MgAl2O4 spinel ceramics by double-doped CeO2 and La2O3