Abstract:Calcium aluminate phases have a particular effect on the early heat release during setting initiation and have a substantial influence on the further workability of ordinary Portland cement. The nature of the calcium aluminate hydration products and its kinetics strongly depends on sulfate content and humidity. The effect of mineralisers on melt formation and viscosity is well described for calcium silicate systems, but information is still lacking for calcium aluminates. Therefore, the synergistic effect on the crystal structure and hydration mechanism of the tricalcium aluminate phase of the addition of mineralizers, i.e. Li 2 O, CuO, SO 3 to the raw meal is here investigated. Co-doped calcium aluminate structures were formed during high-temperature treatment. Thermal analysis (TG–DTA and heating microscopy) was used to describe the ongoing high-temperature reaction. Resulting phase composition was dependent on the concentration of the mineralizer. While phase pure system was prepared with low mineralizer concentrations, with increasing mineralizer content the secondary phases were formed. Raman spectroscopy and XPS analysis were used to investigate the cation substitution and to help describe the cations bonding in co-doped calcium aluminate system. Prepared powders have been hydrated in a controlled manner at different temperatures (288, 298, 308 K). The resulting calorimetric data have been used to investigate the hydration kinetics and determine the rate constant of hydration reaction. First-order reaction (FOR) model was here applied for the activation energy and frequency factor calculations. The metastable and stable calcium aluminate hydrates were formed according to initial phase composition. In phase pure systems with low S content, the formation of stable and metastable hydrates was depended on the reaction temperature. Conversely, in systems with secondary phases and higher S content, the hydration mechanism resembled that which appears in calcium sulfoaluminates.

Effect of hydromagnesite on the hydration of hydratable alumina and properties of corundum-based castables

Effect of the hydrotalcite formation on the fracture behavior and corrosion resistance of HA‐bonded alumina‐spinel castables

Effect of grinding on the hydration of hydratable alumina and properties of hydratable alumina-bonded castables

Hydration behavior and microstructural evolution of hydratable alumina with different particle size in alumina-spinel castables

Influence of magnesium-aluminum hydrotalcite on the microstructure and mechanical properties of magnesia castables

Gas permeability of alumina‐spinel refractory castables bonded with hydratable magnesium carboxylate

Effect of magnesium aluminum hydrotalcite on the properties of CAC-bonded castables

Mechanical properties of refractory castables bonded with hydratable magnesium carboxylate-boric acid

Investigations on phase constitution, mechanical properties and hydration kinetics of aluminous cements containing magnesium aluminate spinel

Enhanced thermal shock resistance of hydratable magnesium carboxylate bonded castables via in-situ formation of micro-sized spinel

Influence of mono-carbonate hydrates on mechanical properties of CAC bonded castables fired at 800 °C

Reconstruction and hydration of hydrotalcite response to thermal activation temperature: Enhancement of properties for magnesia castables

Effects of Bauxite Tailings and Sodium Silicate on Mechanical Properties and Hydration Mechanism of Magnesium Phosphate Cement

Improving the mechanical property of the castables bonded with hydratable magnesium carboxylate by incorporating MgO fumes

Influence of Low-Grade Bauxite on the Properties of Magnesium Phosphate Cement

Hydration mechanism and sintering characteristics of hydratable alumina with microsilica addition

The Influence of Mayenite Employed as a Functional Component on Hydration Properties of Ordinary Portland Cement

Influence of bonding systems on the properties of Al 2 O 3 -MgO refractory castables: Aluminate cement and alumina silica gel

Hydration kinetics of C3A: effect of lithium, copper and sulfur-based mineralizers

Effect of amorphous aluminum hydroxide on the phosphogypsum-based cementitious materials in prefabricated building field

Hydration of high alumina cement–silica fume composite with addition of Portland cement or sodium polyphosphate under hydrothermal treatment