Crack-free caustic magnesia-bonded refractory castables
V.C. Miguel,D.S. Fini,V.S. Pinto,M.H. Moreira,V.C. Pandolfelli,A.P. Luz
DOI: https://doi.org/10.1016/j.ceramint.2021.03.036
IF: 5.532
2021-06-01
Ceramics International
Abstract:<p>A growing interest in designing high-alumina MgO-bonded refractory castables has been identified in recent years due to the magnesia ability to react: (i) with water at the initial processing stages of these materials (inducing the precipitation of brucite phase) or (ii) with alumina, giving rise to <em>in situ</em> MgAl<sub>2</sub>O<sub>4</sub> generation at high temperatures. Nevertheless, despite the great potential of caustic magnesia to be used as a binder in such systems due to its high reactivity, it is still a challenge to control the hydration reaction rate of this oxide and the negative effects derived from the expansive feature of Mg(OH)<sub>2</sub> formation. Thus, this work evaluated the incorporation of different contents of aluminum hydroxyl lactate (AHL) into caustic magnesia-bonded castables, aiming to control the brucite precipitation during the curing and drying steps of the prepared samples, resulting in crack-free refractories. The designed compositions were characterized via flowability, setting behavior, X-ray diffraction, cold flexural strength, porosity, permeability and thermogravimetric measurements. According to the results, instead of Mg(OH)<sub>2</sub>, hydrotalcite-like phases [Mg<sub>6</sub>Al<sub>2</sub>(OH)<sub>16</sub>(OH)<sub>2</sub>.4.5H<sub>2</sub>O and Mg<sub>6</sub>Al<sub>2</sub>(OH)<sub>16</sub>(CO<sub>3</sub>)·4H<sub>2</sub>O] were the main hydrated phases identified in the AHL-containing compositions. The addition of 1.0 wt% of aluminum hydroxyl lactate to the designed castable proved to be, so far, the best option for this magnesia source, resulting in the development of a crack-free refractory with enhanced properties and greater spalling resistance under heating.</p>
materials science, ceramics