Fundamentals of Silico-Ferrite of Calcium and Aluminum (SFCA) and SFCA-I Iron Ore Sinter Bonding Phase Formation: Effects of MgO on Phase Formation During Heating

Nathan A. S. Webster,Mark I. Pownceby,James R. Manuel,Rachel Pattel,Justin A. Kimpton

DOI: https://doi.org/10.1007/s11837-020-04430-y

2020-10-27

JOM

Abstract:The effect of MgO on the stability, concentrations and formation mechanisms of silico-ferrite of calcium and aluminum (SFCA and SFCA-I) iron ore sinter bonding phases during heating in synthetic mixtures was investigated using in situ x-ray diffraction. The novelty of this study is in the intricate detail in which the formation mechanisms of the SFCA-I and SFCA phases are characterized, and the observation of the effects of MgO addition on intermediate phases. For example, the significant mechanistic effect of increasing MgO content is the lack of additional SFCA formed after SFCA-I decomposition, with additional magnesioferrite spinel being formed instead. In MgO-free mixtures, the decomposition of SFCA-I typically results in a significant increase in SFCA concentration. Through the results of phase equilibria experiments, this study also provides evidence that the SFCA-I structure accommodates more Mg2+ than the SFCA structure, which is consistent with evidence that the SFCA-I structure contains a higher amount of Fe2+ than SFCA.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy