Abstract:As part of a systematic investigation into the ternary system CaO-Fe 2 O 3 -SiO 2 , we discovered a phase with a general chemical composition of A 14 O 20 (where A represents Ca, Fe, and Si) and previously unknown symmetry. Synthesis experiments were conducted at 1200 °C in air with an oxide ratio of CaO:Fe 2 O 3 :SiO 2 = 3:5:1 in the starting mixture. In addition to β-Ca 2 SiO 4 , and hematite (Fe 2 O 3 ), powder X-ray diffraction analysis indicated the presence of compounds related to the aluminum-free counterpart of a silico-ferrite of calcium and aluminum (SFCA), one of the major bonding phases in iron ore sinter. Single crystals of this so-called SFC phase, large enough for diffraction experiments, were found in the sintered pellet fragments under a digital microscope. The compound with composition Ca 2.68 Fe 10.32 Si 1.00 O 20 crystallizes in space group I 2/ c and has the following basic crystallographic data: a = 10.4643(10) Å, b = 15.2740(11) Å, c = 5.3050(5) Å, β = 110.017(9)°, V = 796.69(13) Å 3 and Z = 2. The final composition, as determined by crystal structure refinement, differs slightly from the weight-specified starting mixture of Ca 3 Fe 10 SiO 20 and suggests the presence of both Fe(III) and small amounts of Fe(II) in the sample. The crystal structure is related to that of the triclinic polytype-1A of SFC, but exhibits a higher degree of disorder due to the partial occupation of additional octahedrally and tetrahedrally coordinated sites. This results in a smaller unit cell and an increased space-group symmetry. The described phase can be regarded as a basic or family structure, from which the two simplest polytypes (1A and hypothetical 2M) can be derived through ordering processes of cations among different possible vacancies. The chemical similarity to one of the phases of the SFCA-family suggests that such disordered compounds could also occur in industrial sinters.

Experimental Phase Equilibria Studies in the FeO-Fe2O3-CaO-SiO2 System in Air: Results for the Iron-Rich Region

Experimental Phase Equilibria Studies in the FeO-Fe2O3-CaO-Al2O3 System in Air

Experimental Liquidus Studies of the Pb-Fe-Ca-O System in Air

Phase equilibria studies in the CaO–SiO 2 –Al 2 O 3 –MgO system with CaO/SiO 2 ratio of 0.9

Phase Equilibria Studies for CaO–SiO2-5wt.%MgO–Al2O3–TiO2 System in High Al2O3 Content Area with W(cao)/w(sio2) Ratio of 1.50

Phase diagram of V2O3-FetO-SiO2-CaO(15 mass%) system at 1623 K

Experimental Determination of the 1300 °C and 1400 °C Isotherms for CaO–SiO2–TiO2-10 Wt% Al2O3 System in Air

New understanding on formation mechanism of CaFe2O4 in Fe2O3 -Fe3O4-CaO-SiO2 system during sintering Process: Phase transformation and morphologies evolution

Experimental investigation of the phase relations in the SiO2-Dy2O3-CaO ternary system

Fundamentals of Silico-Ferrite of Calcium and Aluminum (SFCA) and SFCA-I Iron Ore Sinter Bonding Phase Formation: Effects of MgO on Phase Formation During Heating

Phase Equilibria of the SiO2–V2O5 system

Phase equilibrium occurring during low-carbon iron-based melt deoxidation with silicostrontium

Phase equilibria of the Na2O‐TiO2‐SiO2 system between 900 and 1600°C in air

Ca2.68Fe10.32Si1.00O20 - a strongly disordered SFCA-related phase in the system CaO-Fe2O3-SiO2

A Thermochemical Data Base for Phase Equilibria in the System Fe-Mg-Si-O at High Pressure and Temperature

Thermodynamic descriptions of the CaO–Al2O3 and CaO–Al2O3–SiO2 systems over the whole composition and temperature ranges

Internally Consistent Thermodynamic Data and Equilibrium Phase Relations for Compounds in the System MgO‐SiO2 at High Pressure and High Temperature

Phase Equilibrium Investigation for CaO-SiO2-5wt.%MgO-20wt.%Al2O3-TiO2 System Relevant to Ti-bearing Slag System

Phase Equilibria Study of the MgO–CaO–SiO2 Slag System with Ferronickel Alloy, Solid Carbon, and Al2O3 Additions

Isothermal Phase Diagram of CaO-SiO2-Nb2O5-5 wt.% Fe2O3-TiO2 System at 1100 °C

Competitive Formation Behavior of Calcium Silicate and Calcium Ferrite in Sintering of Iron Ore Fines