Abstract:Reasonable slag fluidity is essential for stable HIsmelt process operation. During the slag-tapping process, crystallization will cause the slag viscosity to rise sharply, which is not conducive to stable slag-tapping operation, especially for smelting high-titanium slag. In this paper, the viscosity of the CaO-MgO-Al2O3-SiO2-TiO2-FeO slag with varying 10–50% TiO2 content was studied in the laboratory. The crystalline phases of water quenched slag samples at different temperatures were determined by XRD, and it was verified with the results of Factsage thermodynamic calculations. In addition, the effects of crystalline phase, crystalline morphology and crystal size on the critical viscosity of slag were discussed through SEM-EDS analysis. The results show that the proper TiO2 content in the slag is below 40%, the temperature of critical viscosity (Tcv) of the slag is between 1336 °C and 1360 °C, and the Tcv of the slag with a TiO2 content of 50% increases to 1500 °C. The sudden increase in viscosity is related to the crystallization behavior of the slag. With the increase of TiO2 content, the main precipitated titanium-rich phase in the slag changed from dendritic perovskite to plate-shaped pseudobrookite. Among them, when the TiO2 content is 10%, the sharp increase in viscosity of the slag is mainly determined by the precipitation amount of melilite. The amount of crystals in the slag between 20% and 43% causes the viscosity of the slag to rise rapidly, which is mainly due to the fact that the granular crystals have a greater influence on the viscosity than the plate crystals. Compared with the experimental results, it is found that Factsage software cannot accurately calculate the phase equilibrium of slag with a TiO2 content of 40–50%.

Isothermal Phase Diagram of CaO-SiO2-Nb2O5-5 wt.% Fe2O3-TiO2 System at 1100 °C

Phase Equilibrium Investigation for CaO-SiO2-5wt.%MgO-20wt.%Al2O3-TiO2 System Relevant to Ti-bearing Slag System

Experimental Determination of the 1300 °C and 1400 °C Isotherms for CaO–SiO2–TiO2-10 Wt% Al2O3 System in Air

Effect of Al2O3 Addition on the Phase Equilibria Relations of CaO-SiO2-5 Wt%mgo-Al2o3-tio2 System Relevant to Ti-bearing Blast Furnace Slag

Phase equilibria relations in the V2O5-rich part of the Fe2O3-TiO2-V2O5 system at 1200°C related to converter vanadium-bearing slag

The Phase Diagram of a CaO-Al2O3-VOx Slag System under Argon Atmosphere at 1500 °C

Phase Equilibria Study of the MgO–CaO–SiO2 Slag System with Ferronickel Alloy, Solid Carbon, and Al2O3 Additions

Phase equilibria of the Na2O‐TiO2‐SiO2 system between 900 and 1600°C in air

Phase Equilibria Studies for CaO–SiO2-5wt.%MgO–Al2O3–TiO2 System in High Al2O3 Content Area with W(cao)/w(sio2) Ratio of 1.50

Phase Diagram of CaO-Al2O3-VOx Slag System Under Reducing Atmosphere

Phase diagram of V2O3-FetO-SiO2-CaO(15 mass%) system at 1623 K

Influence of TiO2 on the liquidus temperature and structure of CaO-SiO2-Fe2O3-TiO2 slags

The Interface Characteristics of High-Temperature Melt of CaO-Al2O3-MgO-SiO2 System

Phase equilibria of CaO–SiO2–CaF2–P2O5–Ce2O3 system and formation mechanism of britholite

Phase equilibria in the TiO2–Nb2O5 system: New experiments and thermodynamic modeling

Experimental investigation of the phase relations in the SiO2-Dy2O3-CaO ternary system

Experimental Phase Equilibria Studies in the FeO-Fe2O3-CaO-SiO2 System in Air: Results for the Iron-Rich Region

Viscosity of CaO-MgO-Al2O3-SiO2-TiO2-FeO slag with varying TiO2 content: The Effect of Crystallization on Viscosity Abrupt Behavior

Thermophysical Properties of CaO–SiO2–Al2O3–MgO–TiO2–FeOx–V2O3 Slag with CaO/SiO2 = 1.13 with Different TiO2 and V2O3 Additions

The Influence of SiO2 on the Extraction of Ti Element from Ti‐bearing Blast Furnace Slag

The Study on the Interface Reaction Characteristics of Different Binary Slag, CaO – MgO, Al 2 O 3 – CaO, Al 2 O 3 – MgO, SiO 2 – CaO, SiO 2 - MgO