Abstract:Reasonable slag fluidity is essential for stable HIsmelt process operation. During the slag-tapping process, crystallization will cause the slag viscosity to rise sharply, which is not conducive to stable slag-tapping operation, especially for smelting high-titanium slag. In this paper, the viscosity of the CaO-MgO-Al2O3-SiO2-TiO2-FeO slag with varying 10–50% TiO2 content was studied in the laboratory. The crystalline phases of water quenched slag samples at different temperatures were determined by XRD, and it was verified with the results of Factsage thermodynamic calculations. In addition, the effects of crystalline phase, crystalline morphology and crystal size on the critical viscosity of slag were discussed through SEM-EDS analysis. The results show that the proper TiO2 content in the slag is below 40%, the temperature of critical viscosity (Tcv) of the slag is between 1336 °C and 1360 °C, and the Tcv of the slag with a TiO2 content of 50% increases to 1500 °C. The sudden increase in viscosity is related to the crystallization behavior of the slag. With the increase of TiO2 content, the main precipitated titanium-rich phase in the slag changed from dendritic perovskite to plate-shaped pseudobrookite. Among them, when the TiO2 content is 10%, the sharp increase in viscosity of the slag is mainly determined by the precipitation amount of melilite. The amount of crystals in the slag between 20% and 43% causes the viscosity of the slag to rise rapidly, which is mainly due to the fact that the granular crystals have a greater influence on the viscosity than the plate crystals. Compared with the experimental results, it is found that Factsage software cannot accurately calculate the phase equilibrium of slag with a TiO2 content of 40–50%.

Effect of Al2O3 Addition on the Phase Equilibria Relations of CaO-SiO2-5 Wt%mgo-Al2o3-tio2 System Relevant to Ti-bearing Blast Furnace Slag

Phase Equilibrium Investigation for CaO-SiO2-5wt.%MgO-20wt.%Al2O3-TiO2 System Relevant to Ti-bearing Slag System

Effect of Al2o3 Addition on the Precipitated Phase Transformation in Ti-Bearing Blast Furnace Slags

Phase Equilibria Studies for CaO–SiO2-5wt.%MgO–Al2O3–TiO2 System in High Al2O3 Content Area with W(cao)/w(sio2) Ratio of 1.50

Experimental Determination of the 1300 °C and 1400 °C Isotherms for CaO–SiO2–TiO2-10 Wt% Al2O3 System in Air

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Combined Effect of SiO2 and O2 on the Crystallization Behavior of Modified Ti-Bearing Blast Furnace Slag

Effect of W(mgo)/w(al2o3) Ratio and Basicity on Microstructure and Metallurgical Properties of Blast Furnace Slag

Thermophysical Properties of CaO–SiO2–Al2O3–MgO–TiO2–FeOx–V2O3 Slag with CaO/SiO2 = 1.13 with Different TiO2 and V2O3 Additions

Evaluating the Effect of MgO/Al2O3 Ratio on Thermal Behaviors and Structures of Blast Furnace Slag with Low Carbon Consumption

Isothermal Phase Diagram of CaO-SiO2-Nb2O5-5 wt.% Fe2O3-TiO2 System at 1100 °C

The Influence of SiO2 on the Extraction of Ti Element from Ti‐bearing Blast Furnace Slag

Viscosity of CaO-MgO-Al2O3-SiO2-TiO2-FeO slag with varying TiO2 content: The Effect of Crystallization on Viscosity Abrupt Behavior

Effect of B2O3 on the Melting Temperature and Viscosity of CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3 Slag

Influence of TiO2, Al2O3, and Basicity on Viscosity and Structure of High Titanium-Bearing Blast Furnace Slag

Effects of TiO2 and CaO/Al2O3 on Melting Characteristics, Surface Tension, and Structure Electroslag‐Remelting‐Type Low‐Fluorine Slag

The Interface Characteristics of High-Temperature Melt of CaO-Al2O3-MgO-SiO2 System

Effect of CeO2 Content on Melting Performance and Microstructure of CaO-Al2O3-SiO2-MgO Refining Slag

Thermophysical properties of liquid CaO-SiO2-Al2O3-MgO-TiO2-V2O3 slags

Influence of TiO2 on the liquidus temperature and structure of CaO-SiO2-Fe2O3-TiO2 slags

Precipitation Behaviour of Ti Enriched Phase in Ti Bearing Slag