Abstract:In order to transform the crystalline form of Ca2SiO4 (C2S) in phosphorus-containing slag from monoclinic β-polycrystalline to square γ-polycrystalline, a volume expansion of about 11% was generated, which caused the phosphorus-containing slag to undergo self-powdering. The CaO-SiO2-Al2O3-MgO-MnO-P2O5-FeO slag system was analyzed using FactSage7.1 thermodynamic software, and the effects of different P2O5, FeO and basicity on the mineral phase composition of slag system were analyzed in the range of 1300~1700 °C. It was shown that P2O5, FeO and basicity all have an effect on the composition of the mineral phases. When the mass fraction of P2O5 in the slag was lower than 0.25%, it had less effect on the transformation of C2S crystalline structure. When the P2O5 content was higher than 0.25%, it was favorable to the generation of low-melting-point substances, but the P2O5 in the slag reacted with C2S in the silicate phase, making P5+ solidly soluble in C2S, inhibiting the transformation of β-C2S to γ-C2S and hindering the self-powdering of the slag. The FeO content in the slag system ranged from 20% to 28%, and as the FeO content increased, the C2S content in the silicate phase decreased from 33.3% to 25.9%, while the temperature at which the silicate was completely dissolved into the liquid phase decreased from 1600 °C to 1500 °C and the complete melting temperature of the slag decreased. The low FeO content facilitates the self-powdering of slag. In the high-phosphorus slag, at temperatures below 1450 °C, with the increase of basicity, the proportion of C2S in the silicate phase first increased and then decreased. With basicity at 1.8; the highest content of silicate phase, accounting for 33.7%; and the temperature exceeding 1450 °C, the silicate phase dissolved into the liquid phase, which is conducive to the removal of phosphorus from the slag, achieving the self-powdering of high-phosphorus slag.

Phase equilibria of CaO–SiO2–CaF2–P2O5–Ce2O3 system and formation mechanism of britholite

Thermodynamics and kinetics of REEs in CaO–SiO2–CaF2–Ce2O3 system: A theoretical basis toward sustainable utilization of REEs in REE-Bearing slag

Phase Equilibrium Investigation for CaO-SiO2-5wt.%MgO-20wt.%Al2O3-TiO2 System Relevant to Ti-bearing Slag System

Carbothermal Reduction, Melting Separation, and Structural Analysis of Carbon-bearing Rare Earth Iron Ore Pellets

Isothermal Phase Diagram of CaO-SiO2-Nb2O5-5 wt.% Fe2O3-TiO2 System at 1100 °C

Experimental investigation of the phase relations in the SiO2-Dy2O3-CaO ternary system

Experimental constraints on miscibility gap between apatite and britholite and REE partitioning in an alkaline melt

Thermodynamic Analysis of Mineral Phase Composition of Steel Slag System

Experimental Determination of the 1300 °C and 1400 °C Isotherms for CaO–SiO2–TiO2-10 Wt% Al2O3 System in Air

Microstructure characterization and formation mechanism of lanthanum phosphide in FeCrAlRE alloy with ultra-low oxygen

Investigation of the Effect of P2O5 and CaF2 on the Crystallization Behavior of La2O3-bearing Calcium–silicate–aluminum Slags Using the Single Hot Thermocouple Technique

Effect of Al2O3 Addition on the Phase Equilibria Relations of CaO-SiO2-5 Wt%mgo-Al2o3-tio2 System Relevant to Ti-bearing Blast Furnace Slag

Phase equilibria relations in the V2O5-rich part of the Fe2O3-TiO2-V2O5 system at 1200°C related to converter vanadium-bearing slag

Effect of CeO2 Content on Melting Performance and Microstructure of CaO-Al2O3-SiO2-MgO Refining Slag

Kinetics and mechanism of hydrochloric acid leaching of rare earths from Bayan Obo slag and recovery of rare earth oxalate and high purity oxides

Experimental Phase Equilibria Studies in the FeO-Fe2O3-CaO-SiO2 System in Air: Results for the Iron-Rich Region

The study on the reconstruction and evolution pathway of free lime by hot stage mixing molten ironmaking and steelmaking slags in a laboratory

Phase equilibria and thermodynamic assessment of the Al2O3-SiO2-Sc2O3 system

Insight into the mechanism on co-leaching of REEs and Fe from NdFeB sludge: Elucidating phase transformation and co-leaching kinetics

Li-Distribution in Compounds of the Li2O-MgO-Al2O3-SiO2-CaO System—A First Survey

The Phase Diagram of a CaO-Al2O3-VOx Slag System under Argon Atmosphere at 1500 °C