Abstract:<h3 class="a-plus-plus">Abstract</h3> To concentrate vanadium dissolved in steelmaking slag and to separate the obtained vanadium (V)-concentrating phase by a magnetic method, the mineral phases in a CaO-SiO2-MgO-FeOt-Al2O3-V2O3-P2O5 system at 1573 K (1300 °C) were characterized by scanning-electron microscopy-energy-dispersive spectroscopy and X-ray diffractometry. When the samples were equilibrated in a pure iron crucible and argon atmosphere, four phases were identified, namely, orthosilicate, V-bearing spinel, wüstite, and a glass phase. The orthosilicate, V-bearing spinel, and glass phase occurred in all samples, whereas wüstite appeared only in samples with a higher basicity or high FeOt content. The results indicate that the V-bearing spinel phase, which is analogous to Fe3O4, is a thermodynamically stable phase that is suitable for the enrichment of vanadium dissolved in slags. Further analysis reveals that the increases in contents of FeOt and MgO in slag favor spinel-phase formation. When the slags are saturated by the wüstite phase, almost all dissolved vanadium can be concentrated in the spinel phase.

Phase Equilibria of the SiO2–V2O5 system

Phase diagram of V2O3-FetO-SiO2-CaO(15 mass%) system at 1623 K

EXPERIMENTAL STUDY ON THE PHASE RELATIONS OF THE SYSTEM Mg2SiO4-MgAl2O4 AT HIGH PRESSURE AND HIGH TEMPERATURE

Phase equilibrium studies in V 2 O 5 ‐Fe 2 O 3 and V 2 O 5 ‐TiO 2 systems

Phase equilibria relations in the V2O5-rich part of the Fe2O3-TiO2-V2O5 system at 1200°C related to converter vanadium-bearing slag

The Phase Diagram of a CaO-Al2O3-VOx Slag System under Argon Atmosphere at 1500 °C

Phase equilibria of the Na2O‐TiO2‐SiO2 system between 900 and 1600°C in air

Phase equilibria studies in the CaO–SiO 2 –Al 2 O 3 –MgO system with CaO/SiO 2 ratio of 0.9

Phase Equilibria Studies for CaO–SiO2-5wt.%MgO–Al2O3–TiO2 System in High Al2O3 Content Area with W(cao)/w(sio2) Ratio of 1.50

Phase Diagram of CaO-Al2O3-VOx Slag System Under Reducing Atmosphere

Experimental investigation of the phase relations in the SiO2-Dy2O3-CaO ternary system

Experimental Phase Equilibria Studies in the FeO-Fe2O3-CaO-SiO2 System in Air: Results for the Iron-Rich Region

Experimental Determination of the 1300 °C and 1400 °C Isotherms for CaO–SiO2–TiO2-10 Wt% Al2O3 System in Air

Solid-state reaction of a CaO-V2O5 mixture: A fundamental study for the vanadium extraction process

Phase equilibria and thermodynamic assessment of the Al2O3-SiO2-Sc2O3 system

The phase diagram and phase transition of the V2O3−V2O5, system

Phase Equilibrium Investigation for CaO-SiO2-5wt.%MgO-20wt.%Al2O3-TiO2 System Relevant to Ti-bearing Slag System

Phase Equilibria in the Li–V–O System (an Analytical Review)

Internally Consistent Thermodynamic Data and Equilibrium Phase Relations for Compounds in the System MgO‐SiO2 at High Pressure and High Temperature

Experimental Study on the Formation of V-Rich Spinel Phase in CaO-SiO2-MgO-FeOt-Al2O3-V2O3-P2O5 Slags at 1573 K (1300 °C)

Phase Equilibria and Phase Diagram of the Quaternary NaOH–Na 3 VO 4 –Na 2 WO 4 –H 2 O System at 278.15 K to 353.15 K