Experimental Study on the Formation of V-Rich Spinel Phase in CaO-SiO2-MgO-FeOt-Al2O3-V2O3-P2O5 Slags at 1573 K (1300 °C)

Liushun Wu,Cunjun Qi,Baijun Yan,Jue Wang,Yuanchi Dong

DOI: https://doi.org/10.1007/s11663-018-1486-2

2019-01-02

Metallurgical and Materials Transactions B

Abstract:<h3 class="a-plus-plus">Abstract</h3> <p class="a-plus-plus">To concentrate vanadium dissolved in steelmaking slag and to separate the obtained vanadium (V)-concentrating phase by a magnetic method, the mineral phases in a CaO-SiO<sub class="a-plus-plus">2</sub>-MgO-FeO<sub class="a-plus-plus">t</sub>-Al<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub>-V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub>-P<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> system at 1573 K (1300 °C) were characterized by scanning-electron microscopy-energy-dispersive spectroscopy and X-ray diffractometry. When the samples were equilibrated in a pure iron crucible and argon atmosphere, four phases were identified, namely, orthosilicate, V-bearing spinel, wüstite, and a glass phase. The orthosilicate, V-bearing spinel, and glass phase occurred in all samples, whereas wüstite appeared only in samples with a higher basicity or high FeO<sub class="a-plus-plus">t</sub> content. The results indicate that the V-bearing spinel phase, which is analogous to Fe<sub class="a-plus-plus">3</sub>O<sub class="a-plus-plus">4</sub>, is a thermodynamically stable phase that is suitable for the enrichment of vanadium dissolved in slags. Further analysis reveals that the increases in contents of FeO<sub class="a-plus-plus">t</sub> and MgO in slag favor spinel-phase formation. When the slags are saturated by the wüstite phase, almost all dissolved vanadium can be concentrated in the spinel phase.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering