Separation of V-bearing phase from the vanadium slag system utilizing supergravity

Weijun Huang,Yajing Liu,Dong Xu

DOI: https://doi.org/10.1051/metal/2020051

2020-01-01

Abstract:The crystallization and separation behaviors of the V-spinel phase in the FeO-SiO 2 -V 2 O 3 -TiO 2 system as the main components of vanadium slag were investigated to effectively concentrate and separate vanadium from the vanadium slag. Fine V-spinel precipitates were transformed into large lumps and strip crystals by decreasing the temperature from 1773 K to 1723 K. Ti-spinel phases began to crystallize from the molten slag by further decreasing the temperature to 1673 K. In order to adequately precipitate a single V-spinel phase with suitable grain size in the crystals from the molten slag, the temperature was chosen as 1723 K. With introduction of supergravity technology, the Ti-containing slag melt went through the filter to form the Ti-containing slag, while V-spinel crystals were intercepted by the filter to form the V-enriched slag. Consequently, with G = 700 at 1723 K for 10 minutes, the mass fraction of V 2 O 3 was increased from 17.00 wt% before separation to 32.98 wt% in the enriched slag; the recovery ratio of V 2 O 3 reached about 86.50%. In addition, the mass fraction of TiO 2 reached about 19.41 wt% in the Ti-containing slag, which could be recycled as a titanium-bearing material in the metallurgical industry.

metallurgy & metallurgical engineering