Cyclic metallurgical process for extracting V and Cr from vanadium slag: Part I. Separation and recovery of V from chromium-containing vanadate solution

Xue-wen WANG,Ming-e YANG,Yu-qi MENG,Da-xiong GAO,Ming-yu WANG,Zi-bi FU
DOI: https://doi.org/10.1016/s1003-6326(21)65540-1
IF: 3.752
2021-03-01
Transactions of Nonferrous Metals Society of China
Abstract:The separation and recovery of V from chromium-containing vanadate solution were investigated by a cyclic metallurgical process including selective precipitation of vanadium, vanadium leaching and preparation of vanadium pentoxide. By adding Ca(OH)<sub>2</sub> and ball milling, not only the V in the solution can be selectively precipitated, but also the leaching kinetics of the precipitate is significantly improved. The precipitation efficiency of V is 99.59% by adding Ca(OH)<sub>2</sub> according to Ca/V molar ratio of 1.75:1 into chromium-containing vanadate solution and ball milling for 60 min at room temperature, while the content of Cr in the precipitate is 0.04%. The leaching rate of V reaches 99.35% by adding NaHCO<sub>3</sub> into water according to NaHCO<sub>3</sub>/V molar ratio of 2.74:1 to leach V from the precipitate with L/S ratio of 4:1 mL/g and stirring for 60 min at room temperature. The crystals of NH<sub>4</sub>VO<sub>3</sub> are obtained by adjusting the leaching solution pH to be 8.0 with CO<sub>2</sub> and then adding NH<sub>4</sub>HCO<sub>3</sub> according to NH<sub>4</sub>HCO<sub>3</sub>/NaVO<sub>3</sub> molar ratio of 1:1 and stirring for 8 h at room temperature. After filtration, the crystallized solution containing ammonia is reused to leach the precipitate of calcium vanadates, and the leaching efficiency of V is &gt;99% after stirring for 1 h at room temperature. Finally, the product of V<sub>2</sub>O<sub>5</sub> with purity of 99.6% is obtained by calcining the crystals at 560 °C for 2 h.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?