Abstract:Phase equilibria in the Al2O3–Ta2O5 system have been studied by means of CO2 laser heater, high‐speed pyrometer, X‐ray powder diffraction, and scanning electron microscopy. The liquidus and invariant reaction temperatures in the whole composition region were measured by cooling trace tests. The monotectic reaction of Liquid 1→Liquid 2 + Al2O3 was determined to be at about 1547°C, but the typical microstructures for the miscibility gap were not directly observed in our experiments. The tetragonal AlTaO4 phases formed from as‐cast samples were found to congruently melt at 1669°C, and they could maintain stability during the cooling process but would gradually transform into orthorhombic and monoclinic polymorphs after heat treatment. Two eutectic reactions of Liquid → Al2O3 + T‐AlTaO4 and Liquid → T‐AlTaO4 + β‐Ta2O5 were measured to be at 1447°C and 36.7 mol%Ta2O5 and 1513°C and 63.5 mol% Ta2O5, respectively. Due to the undercooling effect, the invariant reaction temperatures determined by this work might be preliminary and need to be verified by more accurate methods. Our experiments confirmed that doping Al2O3 in Ta2O5 phases could improve phase stability of β‐Ta2O5. Finally, thermodynamic optimization of the Al2O3–Ta2O5 system was performed based on the obtained experimental data by means of the CALPHAD method. The self‐consistent thermodynamic parameters are helpful in further efforts for construction of Al2O3–Ta2O5‐based multicomponent thermodynamic database and the development of alumina–tantala‐based materials.

Phase equilibrium studies in V 2 O 5 ‐Fe 2 O 3 and V 2 O 5 ‐TiO 2 systems

Phase Equilibria of the SiO2–V2O5 system

Phase equilibria relations in the V2O5-rich part of the Fe2O3-TiO2-V2O5 system at 1200°C related to converter vanadium-bearing slag

Phase diagram of V2O3-FetO-SiO2-CaO(15 mass%) system at 1623 K

Phase equilibrium investigations of the Al2O3–Ta2O5 system: New experiments and thermodynamic modeling

The phase diagram and phase transition of the V2O3−V2O5, system

Phase equilibria in the TiO2–Nb2O5 system: New experiments and thermodynamic modeling

Phase evolution and thermochromism of vanadium oxide thin films grown at low substrate temperatures during magnetron sputtering

Phase Equilibrium Investigations and Thermodynamic Study of the Y2O3-Ta2O5 System

Phase equilibria of the Na2O‐TiO2‐SiO2 system between 900 and 1600°C in air

Phase equilibria studies in the CaO–SiO 2 –Al 2 O 3 –MgO system with CaO/SiO 2 ratio of 0.9

Experimental Phase Equilibria Studies in the FeO-Fe2O3-CaO-SiO2 System in Air: Results for the Iron-Rich Region

Phase Equilibria Studies for CaO–SiO2-5wt.%MgO–Al2O3–TiO2 System in High Al2O3 Content Area with W(cao)/w(sio2) Ratio of 1.50

Mass Spectrometric Thermodynamic Study of the Fe2O3–TiO2 System

Phase equilibrium investigations and thermodynamic modeling of the HfO2–Ta2O5 system

Effect of CaO addition on phase formation in the Fe-Fe2O3-V2O3 system

Experimental Investigation and Thermodynamic Assessment of Phase Equilibria in the Al-Ta-V Ternary System

Phase Equilibria of the V-Ti-Fe System and Its Applications in the Design of Novel Hydrogen Permeable Alloys

Experimental Investigation of Phase Equilibria in the Ti-Cr-V System at 1000–1200 °C

Experimental Determination of the 1300 °C and 1400 °C Isotherms for CaO–SiO2–TiO2-10 Wt% Al2O3 System in Air

Phase Diagram of CaO-Al2O3-VOx Slag System Under Reducing Atmosphere