Abstract:In order to overcome the serious corrosion problem of furnace hearth refractory materials for smelting reduction ironmaking, the Cr2O3–Al2O3–MgO–ZrO2 refractories were synthesized, and the phase component, microstructure, mechanical characteristics, and slag erosion behavior of composite refractories were investigated and evaluated. The results indicate that the composite refractories mainly consist of Mg(Al, Cr)2O4 spinel phase, (Al, Cr)2O3 solid solution and ZrO2. The content of Mg (Al, Cr)2O4 spinel significantly increases with the increasing MgO content, while the content of (Al, Cr)2O3 obviously decreases. Furthermore, the comprehensive mechanical properties of the MgO modified composite refractories can be obviously enhanced by increasing the MgO content, and sample S4 presents the best mechanical characteristics when the MgO addition is 10 wt%. The corresponding hardness, compressive strength and bending strength are 14.22 GPa, 267.14 MPa and 80.0 MPa, respectively. This is mainly because the formation of Mg(Al, Cr)2O4 significantly improves the densification of composite refractories, and a large number of high-strength Mg (Al, Cr)2O4 spinel “bridge” formed between the large-sized (Al, Cr)2O3 grains. The erosion test results indicate that increasing the MgO content can significantly improve the slag infiltration resistance of composite refractories, because the formation of Mg (Al, Cr)2O4 spinel layer significantly improves the densification of MgO reinforced composite refractories. Although the slag corrosion resistance of Mg(Al, Cr)2O4 is lower than that of (Al, Cr)2O3, the Cr2O3–Al2O3–MgO–ZrO2 refractories still presents good erosion resistance, permeability resistance, and excellent mechanical characteristics.

Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

Synergistic preparation of forsterite‐spinel refractory materials from ferronickel slag and ferrochromium slag

Assessing Magnesia Effect on Preparing Refractory Materials from Ferrochromium Slag

Significant improvement of slag corrosion resistance and thermal shock resistance of corundum‐based dry vibratable refractory by addition of Fe–Si 3 N 4

Preparation and Characterization of MnFe2O4 by a Microwave-Assisted Oxidative Roasting Process

Co-utilization of ferronickel slag and fly ash cenosphere for production of superior thermal insulation materials

Development of Refractory Material from Water Quenched Granulated Ferrochromium Slag

The microstructure evolution and performance enhancement of MgO-C refractories by the addition of MA90 spinel micro-powder

Preparing high-strength ceramsite from ferronickel slag and municipal solid waste incineration fly ash

Simultaneous enhance of the thermal shock resistance and slag-penetration resistance for tundish flow-control refractories: the role of microporous magnesia

Designing low-carbon MgO–Al2O3–La2O3–C refractories with balanced performance for ladle furnaces

Dual roles of Cr2O3 in preparation of glass-ceramics from ferronickel slag

Development of an Ultra-Low Carbon MgO Refractory Doped with α-Al2O3 Nanoparticles for the Steelmaking Industry: A Microstructural and Thermo-Mechanical Study

Implementation of industrial waste ferrochrome slag in conventional and low cement castables: Effect of microsilica addition

Enhanced performance of low-carbon MgO–C refractories with nano-sized ZrO2–Al2O3 composite powder

In-situ crystallization of ferrochrome slag and quartz for preparing cordierite materials

Effect of Phase Composition on Leaching Behavior and Mechanical Properties of Ceramics from Ferrochrome Slag and Tundish Slag

Fabrication and Analysis of Lightweight Magnesia Refractories with Micro-Nanometer Double Pore Size Structure

Behavior of chromium in the reduction and smelting of high alumina nickel laterite in blast furnace

Effect of C/MgO nanocomposite powders on the properties of low-carbon MgO–C refractories

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag