Significant improvement of slag corrosion resistance and thermal shock resistance of corundum‐based dry vibratable refractory by addition of Fe–Si 3 N 4

Gang Qi,Peilin Li,Minghui Li,Ruoyu Chen,Yi Ding,Saisai Li,Siwei Lv,Canhua Li

DOI: https://doi.org/10.1111/jace.19604

IF: 4.186

2023-12-08

Journal of the American Ceramic Society

Abstract:Abstract Fe–Si 3 N 4 was introduced to improve the service performance of corundum‐based dry vibratable refractories in the casting industry, specifically enhancing their thermal shock resistance and resistance to slag corrosion. The study analyzed the effects of Fe–Si 3 N 4 powder content on the refractories’ mechanical properties, phase compositions, slag corrosion resistance, and microstructures. The addition of Fe–Si 3 N 4 facilitated the production of magnesium aluminate spinel in the refractory matrix, while also decreasing the wettability between the molten slag and refractory. Increasing the Fe–Si 3 N 4 content resulted in accelerating the replacing Mg 2+ (0.072 nm) with Al 3+ (0.053 nm) in the spinel. Simultaneously, Fe 3+ (0.055 nm) was effectively dissolved into the alumina crystals. The bulk density, compressive strength, and slag corrosion resistance of the refractories were improved. However, the thermal shock resistance initially increased but then decreased. In industrial tests, a corundum‐based dry vibratable refractory with a 1 wt.% Fe–Si 3 N 4 content effectively prolonged the lifespan of an induction melting furnace when used as a lining refractory. Importantly, the refractory did not spall or generate cracks in the matrix after induction melt furnace industrial test.

materials science, ceramics