Abstract:This study presents a colloidal synthesis method to produce thermoelectric Cu3SbSe4 nanocrystals with high yield. Pb doping is employed to increase carrier concentration and effective mass, confirmed by experimental studies and theoretical calculations. Additionally, lattice distortions and other intriguing nanostructures are found to significantly reduce thermal conductivity. Consequently, the thermoelectric figure of merit zT is greatly enhanced. Developing cost‐effective and high‐performance thermoelectric (TE) materials to assemble efficient TE devices presents a multitude of challenges and opportunities. Cu3SbSe4 is a promising p‐type TE material based on relatively earth abundant elements. However, the challenge lies in its poor electrical conductivity. Herein, an efficient and scalable solution‐based approach is developed to synthesize high‐quality Cu3SbSe4 nanocrystals doped with Pb at the Sb site. After ligand displacement and annealing treatments, the dried powders are consolidated into dense pellets, and their TE properties are investigated. Pb doping effectively increases the charge carrier concentration, resulting in a significant increase in electrical conductivity, while the Seebeck coefficients remain consistently high. The calculated band structure shows that Pb doping induces band convergence, thereby increasing the effective mass. Furthermore, the large ionic radius of Pb2+ results in the generation of additional point and plane defects and interphases, dramatically enhancing phonon scattering, which significantly decreases the lattice thermal conductivity at high temperatures. Overall, a maximum figure of merit (zTmax) ≈ 0.85 at 653 K is obtained in Cu3Sb0.97Pb0.03Se4. This represents a 1.6‐fold increase compared to the undoped sample and exceeds most doped Cu3SbSe4‐based materials produced by solid‐state, demonstrating advantages of versatility and cost‐effectiveness using a solution‐based technology.

An Approach of Enhancing Thermoelectric Performance for P-Type PbS: Decreasing Electronic Thermal Conductivity

Enhanced thermoelectric performance of n -type PbTe bulk materials fabricated by semisolid powder processing

Boosting thermoelectric performance of n-type PbS through synergistically integrating In resonant level and Cu dynamic doping

Thermoelectric enhancement for n-type PbS via synergistic effect of Ti doping and Cu2S compositing

Contrasting Cu Roles Lead to High Ranged Thermoelectric Performance of PbS

Band Engineering Through Pb‐Doping of Nanocrystal Building Blocks to Enhance Thermoelectric Performance in Cu3SbSe4

Contrasting Thermoelectric Transport Behaviors of p -Type PbS Caused by Doping Alkali Metals (Li and Na)

Realizing high-ranged thermoelectric performance in PbSnS2 crystals

Enhanced thermoelectric performance of hot-press Bi-doped n-type polycrystalline PbS

Realization of Valence Band Convergence for High Thermoelectric Performance P-Type PbS

Achieving higher thermoelectric performance of n-type PbTe by adjusting band structure and enhanced phonons scattering

Enhancement of low-temperature thermoelectric performance via Pb doping in Cu3SbSe4

High Performance Thermoelectrics from Earth-Abundant Materials: Enhanced Figure of Merit in PbS by Second Phase Nanostructures.

High Performance Thermoelectrics from Earth-Abundant Materials: Enhanced Figure of Merit in Pbs Through Nanostructuring Grain Size

Lattice expansion enables interstitial doping to achieve a high average ZT in n‐type PbS

Enhancement of thermoelectric performance of Cu 1.98 Se by Pb doping

Thermoelectric transport properties of PbS and its contrasting electronic band structures

Multiscale structure and band configuration tuning to achieve high thermoelectric properties in n-type PbS bulks

Robustly Boosting Thermoelectric Performance of N‐Type PbSe via Lattice Plainification and Dynamic Doping

Contrasting Thermoelectric Transport Properties of n-Type PbS Induced by Adding Ni and Zn

Lattice Plainification Leads to High Thermoelectric Performance of P-Type PbSe Crystals