Abstract:This study presents a colloidal synthesis method to produce thermoelectric Cu3SbSe4 nanocrystals with high yield. Pb doping is employed to increase carrier concentration and effective mass, confirmed by experimental studies and theoretical calculations. Additionally, lattice distortions and other intriguing nanostructures are found to significantly reduce thermal conductivity. Consequently, the thermoelectric figure of merit zT is greatly enhanced. Developing cost‐effective and high‐performance thermoelectric (TE) materials to assemble efficient TE devices presents a multitude of challenges and opportunities. Cu3SbSe4 is a promising p‐type TE material based on relatively earth abundant elements. However, the challenge lies in its poor electrical conductivity. Herein, an efficient and scalable solution‐based approach is developed to synthesize high‐quality Cu3SbSe4 nanocrystals doped with Pb at the Sb site. After ligand displacement and annealing treatments, the dried powders are consolidated into dense pellets, and their TE properties are investigated. Pb doping effectively increases the charge carrier concentration, resulting in a significant increase in electrical conductivity, while the Seebeck coefficients remain consistently high. The calculated band structure shows that Pb doping induces band convergence, thereby increasing the effective mass. Furthermore, the large ionic radius of Pb2+ results in the generation of additional point and plane defects and interphases, dramatically enhancing phonon scattering, which significantly decreases the lattice thermal conductivity at high temperatures. Overall, a maximum figure of merit (zTmax) ≈ 0.85 at 653 K is obtained in Cu3Sb0.97Pb0.03Se4. This represents a 1.6‐fold increase compared to the undoped sample and exceeds most doped Cu3SbSe4‐based materials produced by solid‐state, demonstrating advantages of versatility and cost‐effectiveness using a solution‐based technology.

Lattice expansion enables interstitial doping to achieve a high average ZT in n‐type PbS

High Thermoelectric Efficiency Of N-Type Pbs

Robustly Boosting Thermoelectric Performance of N‐Type PbSe via Lattice Plainification and Dynamic Doping

Realizing Ultrahigh Thermoelectric Performance in n‐Type PbSe Through Lattice Planification and Introducing Liquid‐Like Cu Ions

Synergistically Optimizing Electrical and Thermal Transport Properties of N-Type PbSe

Complex lattice occupation of copper leading to enhanced thermoelectric performance in n-type PbSe

Enhanced Thermoelectric Performance of N‐Type PbSe Through Semi‐Coherent Nanostructure by AgCuTe Alloying

Synergistically Enhancing Thermoelectric Performance of N‐type PbTe with Indium Doping and Sulfur Alloying

Synergistically optimizing carrier and phonon transport properties in n-type PbTe through I doping and SnSe alloying

Enhancement of Thermoelectric Performance for N-Type PbS Via Synergy of CuSbS2 Alloying and Cl Doping

Realizing high-ranged thermoelectric performance in PbSnS2 crystals

Bridging the miscibility gap towards higher thermoelectric performance of PbS

Enhanced Average Power Factor and ZT Value in PbSe Thermoelectric Material with Dual Interstitial Doping

Investigations on Distinct Thermoelectric Transport Behaviors of Cu in N-Type PbS

Thermoelectric enhancement for n-type PbS via synergistic effect of Ti doping and Cu2S compositing

Synergistically optimizing interdependent thermoelectric parameters of n-type PbSe through introducing a small amount of Zn

Enhancing Thermoelectric Performance of p-Type PbSe through Suppressing Electronic Thermal Transports

Enhancement of thermoelectric performance of Cu 1.98 Se by Pb doping

Lattice Plainification Leads to High Thermoelectric Performance of P-Type PbSe Crystals

Band Engineering Through Pb‐Doping of Nanocrystal Building Blocks to Enhance Thermoelectric Performance in Cu3SbSe4

Multiscale structure and band configuration tuning to achieve high thermoelectric properties in n-type PbS bulks