Evaluation of the Long-Term Performance and Durability of Basalt Fiber Reinforced Polymer Bars in Concrete Structures
Chang Su,Xin Wang,Lining Ding,Zheqi Peng,Jingyang Zhou,Zhiyuan Chen,Shui Liu,Zhishen Wu
DOI: https://doi.org/10.1016/j.conbuildmat.2024.138226
IF: 7.4
2024-01-01
Construction and Building Materials
Abstract:To simulate the internal corrosion process of basalt fiber reinforced polymer (BFRP) bars in an alkaline environment of concrete, a diffusion based model was employed and modified in this study according to Fickian diffusion and diffusion coefficients at 25 degree celsius, 40 degree celsius, and 55 degree celsius obtained from existing studies. Thus, the long-term corrosion medium concentration diagram, degraded depth, and strength retention of BFRP bars in the concrete environment at any ambient temperature can be predicted. Durability tests of BFRP bars in an alkaline solution at 60 degree celsius were conducted to verify that the diffusion based model's predictions were accurate. Moreover, long-term bonding tests between BFRP bars and concrete were conducted. The results indicate that the predicted results of the degraded depth and strength degradation of BFRP bars corresponded well to the experimental data. Morphology analysis by scanning electron microscopy (SEM) indicates that the alkaline solution intrusion caused the resin matrix to deteriorate, the fibers and the resin to debond, and the reaction between OH- and SiO2 in the fibers to occur, which in turn caused the tensile and bonding strengths of FRP bars to degrade. Moreover, after 63 days of corrosion at 55 degree celsius, the degraded depth exceeded 7 times that of 25 degree celsius and 2 times that of 40 degree celsius, which implies that the ambient temperature had an obvious influence on the deterioration of BFRPs. The degradation rate was extremely slow at room temperature and rapidly accelerated with the rise in temperature.