Hygrothermal ageing of basalt fiber reinforced epoxy composites

Bo Xiao,Hui Li,Guijun Xian

DOI: https://doi.org/10.1007/978-3-642-17487-2_77

2011-01-01

Abstract:Due to its low price and high chemical resistance, basalt fiber is emerging as a novel reinforcement for fiber reinforced polymer (FRP) composites used in civil engineering in recent years. Compared to widely applied glass fiber based FRP (GFRP) and carbon fiber based FRP (CFRP), however, much less research works on the durability performances of basalt fiber reinforced polymer (BFRP), have been done by now, which seriously hinders its wide and safe application. In the present study, unidirectional basalt fiber fabric reinforced epoxy composites were prepared with a wet lay-up process. Such BFRP materials are expected to be used for external rehabilitation, strengthening or renewal of structures. Durability studies were performed on cured BFRP strips through water, alkali solution immersion at various temperatures. The evolution of the water uptake and mechanical properties with the ageing time was investigated. The aim of the study is to demonstrate the feasibility of using BFRP in severe civil environments, and to disclose the possible degradation mechanisms. As shown, tensile strength of the BFRP samples shows remarkable degradation due to water and alkaline solution immersion, while the tensile modulus is affected slightly. In addition, the mechanical property degradation of the BFRP samples in water is much less than that in alkaline solutions. The results indicate the current basalt fiber need to be modified in its chemical compositions, surface treat-ment for enhanced durability performance.