Abstract:Glass fiber reinforced polypropylene (GFRPP) bending bars have many advantages, such as high toughness, high durability, repeated molding and recycling, which can be used in concrete structures to replace steel stirrup for solving the problems of corrosion and service life. However, the changes in the properties of GFRPP bending bars during long-term use in alkaline concrete environments require further investigation. In the present study, GFRPP bending bars were immersed in alkaline solution at 20°C, 40°C, and 60°C for as long as 180 d. The water absorption, hydrolysis, mechanical properties, and microscopic properties of the bending bars were evaluated to understand the long-term performance and mechanism of degradation. The bending bars had a higher saturated water absorption percentage and time along with a lower diffusion rate than the straight bars due to the presence of pores and micro-cracks formed during the bending process. The dissolution of the glass fibers in alkaline solution led to the partial mass loss of the GFRPP bars. Compared to the control, the tensile strength retention of the bending bars was 20.6%–56.0%. The tensile failure mode changed from fiber bursting before immersion to shear fracture after immersion due to the decreased interfacial bonding strength and increased glass fiber brittleness. The primary degradation mechanisms were the etching of glass fibers, interface debonding, and increased void volume (∼23.7%). The bending bars were more seriously eroded than the straight bars due to the twisting of the fibers and imperfect interfaces. The predicted degradation times of the GFRPP bending bars ranged from 1.7 years (Haikou) to 3.9 years (Harbin), corresponding to a stable tensile strength retention of 22.13%. The results provide a basis for evaluating the durability and service life of GFRPP bending bars and promote the application of GFRPP composite stirrups in concrete structures.

Degradation factors and microstructure degradation characteristics of B/GFRP bars in harsh environment: A review

Environmental Impact on the Durability of FRP Reinforcing Bars

Degradation of Basalt Frp Bars in Alkaline Environment

Prediction of Long-Term Performance and Durability of Bfrp Bars under the Combined Effect of Sustained Load and Corrosive Solutions

Evaluation of the Long-Term Performance and Durability of Basalt Fiber Reinforced Polymer Bars in Concrete Structures

Degradation of GFRP bars in alkaline environments: An experimental and molecular dynamics study

Deterioration mechanism and hardness degradation for GFRP bars used in marine concrete structures

Advances in durability of FRP bars under alkaline environment

Long-Term Durability of Basalt- and Glass-Fibre Reinforced Polymer (bfrp/gfrp) Bars in Seawater and Sea Sand Concrete Environment

Durability and microstructure degradation mechanism of FRP-seawater seasand concrete structures: A review

Experimental study on the durability of BFRP bars embedded in concrete

Study on the Durability of GFRP Bars and Carbon/glass Hybrid Fiber Reinforced Polymer (HFRP) Bars Aged in Alkaline Solution

Durability Assessment of GFRP Bars Embedded in UHP-ECCs Subjected to an Accelerated Aging Environment with Sustained Loading

Prediction of Long-Term Durability of Unidirectional/multidirectional Basalt Fiber- and Hybrid Fiber-Reinforced Polymer Profiles under Concrete Environment

Factors influencing strength loss of glass‐fiber‐reinforced composite bars in highly alkaline environment of concrete

Review on Degradation Behavior of Fiber-Reinforced Polymer Bars in Marine Environments

Durability assessment of GFRP bars exposed to combined accelerated aging in alkaline solution and a constant load

A Review on the Durability of FRP Bars

Long-term Properties Evolution and Life Prediction of Glass Fiber Reinforced Thermoplastic Bending Bars Exposed in Concrete Alkaline Environment

Durability of FRP bars and FRP bar reinforced seawater sea sand concrete structures in marine environments

Effect of sustained load and seawater and sea sand concrete environment on durability of basalt- and glass-fibre reinforced polymer (B/GFRP) bars