Abstract:The corrosion resistance of FRP-reinforced ordinary concrete members under the combined action of harsh environments (i.e., alkaline or acidic solutions, salt solutions) and freeze-thaw cycles is still unclear. To study the mechanical and apparent deterioration of carbon/basalt/glass/aramid fiber cloth reinforced concrete under chemical and freeze-thaw coupling. Plain concrete blocks and FRP-bonded concrete blocks were fabricated. The tensile properties of the FRP sheet and epoxy resin sheet before and after chemical freezing, the compressive strength of the FRP reinforced test block, and the bending capacity of the prismatic test block pasted with FRP on the prefabricated crack side were tested. The deterioration mechanism of the test block was analyzed through the change of surface photos. Based on the experimental data, the Lam-Teng constitutive model of concrete reinforced by alkali-freeze coupling FRP is modified. The results indicate that, in terms of apparent properties, with the increase in the duration of chemical freeze-thaw erosion, the surface of epoxy resin sheets exhibits an increase in pores, along with the emergence of small cracks and wrinkles. The texture of FRP sheets becomes blurred, and cracks and wrinkles appear on the surface. In terms of failure modes, as the number of chemical coupling erosion cycles increases, the location of failure in epoxy resin sheets becomes uncertain, and the failure plane tilts towards the direction of the applied load. The failure mode of FRP sheets remains unchanged. However, the bonding strength between FRP sheets and concrete decreases, resulting in a weakened reinforcement effect. In terms of mechanical properties, FRP sheets undergo the most severe degradation in the coupled environment of acid freeze-thaw cycles. Among them, GFRP experiences the largest degradation in tensile strength, reaching up to 30.17%. In terms of tensile performance, the sheets rank from highest to lowest as follows: CFRP, BFRP, AFRP, and GFRP.As the duration of chemical freeze-coupled erosion increases, the loss rate of compressive strength for specimens bonded with CFRP is the smallest (9.62% in salt freeze-thaw environment), while the loss rate of bearing capacity is higher for specimens reinforced with GFRP (33.8% in acid freeze-thaw environment). In contrast, the loss rate of bearing capacity is lower for specimens reinforced with CFRP (13.6% in salt freeze-thaw environment), but still higher for specimens reinforced with GFRP (25.8% in acid freeze-thaw environment).

Effects of Corrosive Environments on Properties of Pultruded GFRP Plates

Effect of chloride penetration on CFRP sheet, CFRP‐concrete interface, and CFRP‐strengthened concrete beams

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

A comprehensive review on mechanical properties of pultruded FRP composites subjected to long-term environmental effects

Effects of corrosion depths on flexural properties of glass fiber/unsaturated polyester composites in salt spray environment

Influence of seawater sea sand concrete environment on the long‐term tensile properties of pultruded basalt and basalt‐carbon‐hybrid fiber reinforced polymer profiles

Investigation on damage evolution mechanism of various FRP strengthened concrete subjected to chemical-freeze-thaw coupling erosion

Deterioration mechanism and hardness degradation for GFRP bars used in marine concrete structures

Mechanical and dynamic characteristics for the CFRP, GFRP, and hybrid composites exposed to HCl environment

Effect of sustained loads on the durability of GFRP bars with and without UHP-ECC cover

Durability assessment of GFRP bars exposed to combined accelerated aging in alkaline solution and a constant load

Degradation factors and microstructure degradation characteristics of B/GFRP bars in harsh environment: A review

Effect of high‐temperature, high‐pressure, and acidic conditions on the structure and properties of high‐performance fibers

Factors influencing strength loss of glass‐fiber‐reinforced composite bars in highly alkaline environment of concrete

Study on the Durability of GFRP Bars and Carbon/glass Hybrid Fiber Reinforced Polymer (HFRP) Bars Aged in Alkaline Solution

Durability of an Epoxy Resin and Its Carbon Fiber- Reinforced Polymer Composite upon Immersion in Water, Acidic, and Alkaline Solutions

Influence of Hygrothermal Aging on the Durability and Interfacial Performance of Pultruded Glass Fiber-Reinforced Polymer Composites

LONG TERM PERFORMANCE OF PULTRUDED FRP IN DESULFURIZATION ENVIRONMENT OF POWER PLANT

Effect of Corrosive Aging Environments on the Flexural Properties of Silane-Coupling-Agent-Modified Basalt-Fiber-Reinforced Composites

Assessment of Environmental Impact on Glass-Fiber-Reinforced Polymer Pipes Mechanical and Thermal Properties

Combined Effects of Sustained Loads and Wet-Dry Cycles on Durability of Glass Fiber Reinforced Polymer Composites