Abstract:Concrete in coastal areas is susceptible to structural damage caused by corrosion and expansion of reinforcement. Near‐surface mounted (NSM) fiber‐reinforced polymer (FRP) bars have become effective for strengthening damaged reinforced concrete structures. The bonding performance of NSM FRP bars in concrete is a key factor limiting their application and promotion in civil engineering. In this study, the influences of the conditioned environment, such as the chloride salt concentration, immersion time, and bond length of the FRP bar, on the bonding performance were investigated experimentally. First, material properties in a conditioned environment were studied. Subsequently, the failure mode, bond stress–slip curve, and bond strength of the NSM FRP bar in concrete were investigated. Finally, the microstructure and chemical composition of the materials were revealed using scanning electron microscopy and energy‐dispersive spectroscopy (EDS) images of the materials under environmental conditions. The transfer mechanism of NSM FRP bars in concrete with epoxy was revealed. The results showed that the failure modes of the pullout specimens can be divided into epoxy splitting failure and basalt fiber‐reinforced polymer (BFRP) pulling failure. The chloride‐salt concentration was a critical factor affecting the bond properties, and the longer the bond length, the lower the bond strength. The microstructure clearly shows that the degradation of the bonding behavior at the interface of the NSM FRP bar in concrete in a conditioned environment is attributable primarily to the resin damage of the epoxy, resulting in pit corrosion. There was no significant damage to the fibers in the FRP bar, and the degradation was primarily due to resin matrix damage and interfacial debonding. The EDS results showed that the degradation of the epoxy resin and BFRP bars was caused by CO bond and SiO bond fractures, respectively.

Long-Term Bond Durability of Fiber-Reinforced Polymer Bars Embedded in Seawater Sea-Sand Concrete under Ocean Environments

Bond Durability of BFRP Bars Embedded in Concrete under Seawater Conditions and the Long-Term Bond Strength Prediction

Bond durability and degradation mechanism of GFRP bars in seawater sea-sand concrete under the coupling effect of seawater immersion and sustained load

Bond behavior of basalt fiber reinforced polymer bars in seawater sea-sand concrete exposed to daily temperature variations

Long-Term Durability of Basalt- and Glass-Fibre Reinforced Polymer (bfrp/gfrp) Bars in Seawater and Sea Sand Concrete Environment

Durability of BFRP bars and BFRP reinforced seawater sea-sand concrete beams immersed in water and simulated seawater

Durability Performances of Carbon Fiber-Reinforced Polymer and Concrete-Bonded Systems under Moisture Conditions

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Bond Performance between Fiber-Wrapped Ribbed Basalt Fiber-Reinforced Polymer Bars and Seawater Sea-Sand Concrete

Effect of Dry-Wet Cycles on BFRP Bars and Modified Ceramsite Concrete in Marine Environments

Experimental Investigation on the Bond Performance of Sea Sand Coral Concrete with FRP Bar Reinforcement for Marine Environments

Effect of sustained load and seawater and sea sand concrete environment on durability of basalt- and glass-fibre reinforced polymer (B/GFRP) bars

The durability of seawater sea-sand concrete beams reinforced with metal bars or non-metal bars in the ocean environment

Effect of Different Environments on Bond Strength of Glass Fiber-Reinforced Polymer and Steel Reinforcing Bars

Durability study of concrete-covered basalt fiber-reinforced polymer (BFRP) bars in marine environment

Durability Study On Interlaminar Shear Behaviour Of Basalt-, Glass- And Carbon-Fibre Reinforced Polymer (B/G/Cfrp) Bars In Seawater Sea Sand Concrete Environment

Fatigue bond behaviour between basalt fibre-reinforced polymer bars and seawater sea-sand concrete

Bond performance of NSM FRP–concrete interfaces with epoxy under chloride‐salt conditioned environments

Bond durability between BFRP bars and recycled aggregate seawater sea-sand concrete in freezing-thawing environment

Durability of Basalt Fibers, Glass Fibers, and Their Reinforced Polymer Composites in Artificial Seawater

Shear performance degradation of basalt fiber‐reinforced polymer bars in seawater environments: Coupled effects of seawater sea‐sand geopolymer mortar coatings and sustained loading