Abstract:Steel-basalt hybrid fibers reinforced cementitious composite (SBFRCC) is a potential reinforce-ment and repair material for engineering structures with fire risk due to its excellent mechanical properties exposed to ambient and high temperatures. However, the bonding properties between SBFRCC and existing concrete are still unclear, especially at high temperatures. To fill this gap, the bonding properties between SBFRCC and existing concrete at high temperatures were investigated based on two situations by using the slant shear and splitting tensile tests. First, the existing concrete was heated at high temperatures and then bonded with SBFRCC and strengthening concrete to form combined systems, respectively. The effects of the interface roughness, high temperature duration, and post-fire-curing on their bonding properties were investigated. Second, the existing concrete was bonded with SBFRCC and then heated at high temperatures, and the effects of fly ash substation rates on the bonding properties were studied. Besides, the backscattered-electron (BSE) was used to observe the interface between the exiting concrete and SBFRCC exposed to various temperatures. Results show that the first bonded and then heated specimens are slide-failed and separated at the bonding interface from room tem-perature to 600 degrees C, while the damage is generated within the existing concrete at 800 degrees C. SBFRCC has better high temperature resistance than the existing concrete. The slant shear and splitting tensile strengths between PC-A and SBFRCC are 9%-33.3% higher than that of PC-A and strengthening concrete at all temperatures. The appropriate roughness at the interface by pol-ishing can significantly improve the bonding properties between the existing concrete and SBFRCC. The bonding strength is recovered by more than 18.2% and 29.8% after the post-fire curing of 28 and 90 d, respectively. The increase of fly ash substitution rates has a certain contribution to the bonding properties above 600 degrees C.

Bond durability between BFRP bars and recycled aggregate seawater sea-sand concrete in freezing-thawing environment

Bond behaviour of recycled aggregate concrete with basalt fibre-reinforced polymer bars

Bond Durability of BFRP Bars Embedded in Concrete under Seawater Conditions and the Long-Term Bond Strength Prediction

Bond behavior of basalt fiber reinforced polymer bars in seawater sea-sand concrete exposed to daily temperature variations

Dynamic bond behaviour of fibre-wrapped basalt fibre-reinforced polymer bars embedded in sea sand and recycled aggregate concrete under high-strain rate pull-out tests

Study on the bond properties between BFRP bars and hybrid fibers reinforced recycled concrete under freeze-thaw cycles

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Study on the Bonding Performance of BFRP Bars with Seawater Sand Concrete

Bond–Slip Performance of Steel–Fiber-Reinforced Polymer Composite Bars (SFCBs) and Glass Fiber with Expansion-Agent-Reinforced Seawater Sea-Sand Concrete (GF-EA-SSSC) under Freezing–Thawing Environment

Bond Performance between Fiber-Wrapped Ribbed Basalt Fiber-Reinforced Polymer Bars and Seawater Sea-Sand Concrete

Study on bond properties between near-surface mounted BFRP bars and concrete under freeze-thaw cycles in seawater

Fatigue bond behaviour between basalt fibre-reinforced polymer bars and seawater sea-sand concrete

Bond performance of recycled coarse aggregate concrete with rebar under freeze–thaw environment: A review

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Bond strength of GFRP bars to high strength and ultra-high strength fiber reinforced seawater sea-sand concrete (SSC)

Bond performance between hybrid fiber-reinforced concrete and BFRP bars under freeze-thaw cycle

Bond behavior between basalt fiber‐reinforced polymer rebars and coral‐reef‐sand concrete conditioned in saline solution

Effect of Dry-Wet Cycles on BFRP Bars and Modified Ceramsite Concrete in Marine Environments

Bond Behaviour of Normal/Recycled Concrete and Corroded Steel Bars

Durability of BFRP bars and BFRP reinforced seawater sea-sand concrete beams immersed in water and simulated seawater

Bonding Properties Between Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites and Existing Concrete at High Temperatures