Abstract:To study the bond properties between basalt fiber reinforced polymer (BFRP) bars and hybrid fibers which were basalt fiber (BF) and polypropylene fiber (PF) reinforced recycled concrete under freeze-thaw cycles, conducting center pull-out tests to study the effects of three factors on the bond properties: the number of freeze-thaw cycles, the volume fractions of single fiber, and the volume fractions of hybrid fibers. Based on the data obtained from the test, establishing a four-stage bond-slip constitutive relationship model. The results showed that the failure modes were pull-out failure and splitting failure. The bond strength decreased when adding the single fiber, with a maximum reduction of 13.18%, but the peak slip increased, with a maximum increase of 69.92%. When the volume fraction of BF was 0.3%, it achieved the optimal effect. The bond strength and peak slip increased when adding hybrid fibers, with maximum increases of 13.47 and 130.08%, respectively. However, excessive fiber content will reduce the increase of bond strength. The bond strength between BFRP bars and hybrid fiber-reinforced recycled aggregate concrete (HFRAC) increased when the number of freeze-thaw cycles increased but decreased when the number of freeze-thaw cycles exceeded 50. The four-stage bond-slip constitutive relationship model fitted well with the bond-slip curves. Compared with other fiber-reinforced recycled concrete specimens, this model fitted better with the curves of HFRAC specimens after freeze-thaw cycles and had the best fitting effect for the internal crack slip stage of the curves.

What problem does this paper attempt to address?

### Problems the paper attempts to solve This paper aims to study the bond performance between basalt fiber - reinforced polymer (BFRP) bars and recycled concrete reinforced with hybrid fibers (basalt fiber BF and polypropylene fiber PF) under freeze - thaw cycle conditions. Specifically, the author studied the influence of the following three factors on the bond performance through the central pull - out test: 1. **Number of freeze - thaw cycles**: Freeze - thaw cycles are one of the important factors affecting the durability and service life of concrete structures. Research shows that with the increase in the number of freeze - thaw cycles, the mechanical properties of recycled concrete will gradually decline, and the bond performance between BFRP bars and recycled concrete will also be affected. 2. **Volume fraction of single fiber**: The influence of single fibers (BF or PF) with different volume fractions on the bond performance was studied. The results show that adding a single fiber will lead to a decrease in bond strength, but an increase in peak slip. In particular, when the volume fraction of BF is 0.3%, the effect is the best. 3. **Volume fraction of hybrid fibers**: The influence of hybrid fibers (BF + PF) with different volume fractions on the bond performance was studied. The results show that adding hybrid fibers can significantly improve the bond strength and peak slip, but an excessive fiber content will reduce the increase in bond strength. ### Research background Freeze - thaw damage is an important factor affecting the durability and service life of concrete structures. Especially in cold regions, freeze - thaw cycles will cause the concrete surface to peel off and reduce the structural strength. In addition, with the development of the economy and society, the reuse of construction waste has become an important research direction. Using fiber - reinforced recycled concrete to replace ordinary concrete and BFRP bars to replace steel bars can reduce the impact of freeze - thaw cycles on structural safety and bearing capacity. Therefore, studying the bond performance between BFRP bars and fiber - reinforced recycled concrete is of great significance for improving structural performance. ### Main findings - Adding a single fiber (BF or PF) will reduce the bond strength but increase the peak slip. - The addition of hybrid fibers (BF + PF) significantly improves the bond strength and peak slip, and the best effect is achieved when the volume fraction of BF is 0.3%. - An increase in the number of freeze - thaw cycles will first increase and then decrease the bond strength, and the bond strength begins to decline after more than 50 freeze - thaw cycles. - A four - stage bond - slip constitutive relationship model was established, which can fit the experimental data well, especially in the internal crack slip stage. ### Conclusion This study provides an important basis for understanding the bond performance between BFRP bars and hybrid - fiber - reinforced recycled concrete, helps to optimize the mix design of fiber - reinforced recycled concrete, and provides a reference for practical engineering applications.

Study on the bond properties between BFRP bars and hybrid fibers reinforced recycled concrete under freeze-thaw cycles

Bond performance between hybrid fiber-reinforced concrete and BFRP bars under freeze-thaw cycle

Ultimate Strength of Reinforced Concrete Beams Retrofitted with Hybrid Bonded Fiber-Reinforced Polymer

Experimental Investigation on Influence of Embedment Length, Bar Diameter and Concrete Cover on Bond Between Reinforced Bars and Steel Fiber Reinforced Concrete (SFRC)

Bond durability between BFRP bars and recycled aggregate seawater sea-sand concrete in freezing-thawing environment

Investigation of the bond properties between hybrid fiberreinforced concrete and BFRP bars after exposure to high temperature

Study on bond properties between near-surface mounted BFRP bars and concrete under freeze-thaw cycles in seawater

The interfacial bond properties and model for basalt fiber reinforced polymer bar in ultra-high-performance concrete subjected monotonic and reversed cyclic loading

Bond behaviour of recycled aggregate concrete with basalt fibre-reinforced polymer bars

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Bonding Properties Between Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites and Existing Concrete at High Temperatures

Refined Modeling of the Interfacial Behavior Between FRP Bars and Concrete under Different Loading Rates

Study on the Bonding Performance of BFRP Bars with Seawater Sand Concrete

Bond behavior of BFRP bars in concrete under lateral pressure

Experimental and theoretical study on bond behavior of helically wound FRP bars with different rib geometry embedded in ultra-high-performance concrete

The Effects of Hybrid Steel/Basalt Fibers on the Durability of Concrete Pavement against Freeze-Thaw Cycles

Experimental study on the fatigue bond behavior of concrete beams reinforced with hybrid fiber‐reinforced polymer and steel bars

Bond Durability of BFRP Bars Embedded in Concrete under Seawater Conditions and the Long-Term Bond Strength Prediction

Bond behavior of basalt fiber reinforced polymer bars in seawater sea-sand concrete exposed to daily temperature variations

Experimental Study on the Bond Performance between Fiber-Reinforced Polymer Bar and Unsaturated Polyester Resin Concrete

Experimental Investigations on Bond Behavior between FRP Bars and Advanced Sustainable Concrete