Abstract:Steel-basalt hybrid fibers reinforced cementitious composite (SBFRCC) is a potential reinforce-ment and repair material for engineering structures with fire risk due to its excellent mechanical properties exposed to ambient and high temperatures. However, the bonding properties between SBFRCC and existing concrete are still unclear, especially at high temperatures. To fill this gap, the bonding properties between SBFRCC and existing concrete at high temperatures were investigated based on two situations by using the slant shear and splitting tensile tests. First, the existing concrete was heated at high temperatures and then bonded with SBFRCC and strengthening concrete to form combined systems, respectively. The effects of the interface roughness, high temperature duration, and post-fire-curing on their bonding properties were investigated. Second, the existing concrete was bonded with SBFRCC and then heated at high temperatures, and the effects of fly ash substation rates on the bonding properties were studied. Besides, the backscattered-electron (BSE) was used to observe the interface between the exiting concrete and SBFRCC exposed to various temperatures. Results show that the first bonded and then heated specimens are slide-failed and separated at the bonding interface from room tem-perature to 600 degrees C, while the damage is generated within the existing concrete at 800 degrees C. SBFRCC has better high temperature resistance than the existing concrete. The slant shear and splitting tensile strengths between PC-A and SBFRCC are 9%-33.3% higher than that of PC-A and strengthening concrete at all temperatures. The appropriate roughness at the interface by pol-ishing can significantly improve the bonding properties between the existing concrete and SBFRCC. The bonding strength is recovered by more than 18.2% and 29.8% after the post-fire curing of 28 and 90 d, respectively. The increase of fly ash substitution rates has a certain contribution to the bonding properties above 600 degrees C.

Bond behavior of basalt fiber reinforced polymer bars in seawater sea-sand concrete exposed to daily temperature variations

Bond Durability of BFRP Bars Embedded in Concrete under Seawater Conditions and the Long-Term Bond Strength Prediction

Fatigue bond behaviour between basalt fibre-reinforced polymer bars and seawater sea-sand concrete

Bond Performance between Fiber-Wrapped Ribbed Basalt Fiber-Reinforced Polymer Bars and Seawater Sea-Sand Concrete

Bond-Slip Behavior of Basalt Fiber Reinforced Polymer Bar in Concrete Subjected to Simulated Marine Environment: Effects of BFRP Bar Size, Corrosion Age, and Concrete Strength

Dynamic bond behaviour of fibre-wrapped basalt fibre-reinforced polymer bars embedded in sea sand and recycled aggregate concrete under high-strain rate pull-out tests

Bond durability between BFRP bars and recycled aggregate seawater sea-sand concrete in freezing-thawing environment

Experimental Investigation on Influence of Embedment Length, Bar Diameter and Concrete Cover on Bond Between Reinforced Bars and Steel Fiber Reinforced Concrete (SFRC)

Effect of Dry-Wet Cycles on BFRP Bars and Modified Ceramsite Concrete in Marine Environments

Durability of BFRP bars and BFRP reinforced seawater sea-sand concrete beams immersed in water and simulated seawater

Experimental Investigation on the Bond Performance of Sea Sand Coral Concrete with FRP Bar Reinforcement for Marine Environments

Study on the Bonding Performance of BFRP Bars with Seawater Sand Concrete

Bond durability and degradation mechanism of GFRP bars in seawater sea-sand concrete under the coupling effect of seawater immersion and sustained load

Durability study of concrete-covered basalt fiber-reinforced polymer (BFRP) bars in marine environment

Bond behavior between basalt fiber‐reinforced polymer rebars and coral‐reef‐sand concrete conditioned in saline solution

Long-Term Durability of Basalt- and Glass-Fibre Reinforced Polymer (bfrp/gfrp) Bars in Seawater and Sea Sand Concrete Environment

Bond behaviour of recycled aggregate concrete with basalt fibre-reinforced polymer bars

Study on bond properties between near-surface mounted BFRP bars and concrete under freeze-thaw cycles in seawater

Degradation of bond strength and deformation between TRC-confined seawater sand concrete and BFRP bars under chloride corrosion environment

Bond performance of NSM FRP–concrete interfaces with epoxy under chloride‐salt conditioned environments

Bonding Properties Between Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites and Existing Concrete at High Temperatures