Abstract:The use of recycled brick aggregates (RBAs) in concrete could provide sustainable solution in construction industry by reducing the consumption of natural resources and protecting the environment by saving landfill sites. However, the use of RBAs is uncommon due to limited available research studies investigating its mechanical and durability behavior, especially the freeze-thaw (FT) behavior. Despite a few studies on FT resistance of RBA concrete (RBAC), the FT deterioration mechanism in RBAC is not fully understood, particularly at the microscale. This lack of understanding hinders the widespread adoption of RBAC in sustainable construction practices, particularly in cold regions. Therefore, this study investigates the FT deterioration mechanism in RBAC using macro and microscale experiments and proposes a Weibull damage model to accurately describe the damage variation in RBAC. RBAC specimens with different water-cement (w/c) ratios of 0.65, 0.5 and 0.35 and RBA replacement levels of 0%, 25%, 50% and 100% were produced and tested under rapid FT cycles. Surface scaling, mass loss, relative dynamic modulus of elasticity, and compressive strength reduction were evaluated. X-ray computed tomography (XCT) was used to characterize pore structure and microcracking alterations during FT cycles. The results showed that the deterioration of RBAC increased with the increase in RBA replacement level. XCT revealed increased porosity and microcracking within the RBA particles, which was linked to the significant damage observed in RBAC compared to reference concrete. Quantitative analysis of pore size distribution before and after FT cycling revealed a substantial increase in small pores (<1 mm3) in RBAC. The proposed Weibull distribution damage model accurately described the damage variation in RBAC with different w/c ratios. This study provides new insights into multiscale FT deterioration mechanisms affecting RBAC, aiding in optimizing RBAC mix designs to balance sustainability and durability.

Bond performance of recycled coarse aggregate concrete with rebar under freeze–thaw environment: A review

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Bond behavior between deformed steel bars and recycled aggregate concrete after freeze-thaw cycles

Characterizations and Quantification of Freeze-Thaw Behaviors of Recycled Brick Aggregate Concrete

RBSM-based Mesoscale Study of Frost Deterioration for Recycled Concrete Considering Air-Entrainment in Old and New Mortar

Bond durability between BFRP bars and recycled aggregate seawater sea-sand concrete in freezing-thawing environment

An overview of bond behavior of recycled coarse aggregate concrete with steel bar

Frost Resistance of Recycled Aggregate Concrete: A Critical Review

Study on Bonding Property between Steel Rebars and Concrete Caused by Freeze-Thaw Action

Bond Behaviour of Normal/Recycled Concrete and Corroded Steel Bars

Experimental study on bond performance of recycled coarse aggregates concrete with circular steel tubes after freeze–thaw cycling

Evaluation of residual bond behaviour between rebar and recycled aggregate concrete after high-temperature exposure followed by water spray cooling

Coupled Effects of the Freeze-Thaw Cycles and Salt Erosion on the Performance of Recycled Aggregate Concrete

The influence of carbonized recycled fine aggregate on the bond properties between recycled aggregate concrete and corroded rebars

Performance Evolution of Recycled Aggregate Concrete under the Coupled Effect of Freeze-Thaw Cycles and Sulfate Attack

Bonding Properties Between Reinforcing Bars and Concrete Containing Mineral Admixtures in Freeze-Thaw Environment

Bond Behavior Between High-Strength Recycled Aggregate Concrete and UHSSB Using Beam Test

Bond behaviour of recycled aggregate concrete with basalt fibre-reinforced polymer bars

Study on the bond properties between BFRP bars and hybrid fibers reinforced recycled concrete under freeze-thaw cycles

Microstructure of Bonding Interface Between Reinforcement and Concrete in Freeze-thaw Environment

Axial compression performance of slurry‐wrapping recycled aggregate concrete‐filled steel tube short columns under freeze–thaw cycles