Abstract:The salt-frost damage characterization of multiple interfacial transition zones (ITZs) is one of the major concerns for further exploring the durability-related properties of recycled aggregate concrete (RAC) exposed to cold region. The actual service state of RAC structures is often coupled with multiple environments, leading to more complex freeze-thaw damage mechanisms in ITZs. This study adopted the simulant multiple ITZs of RAC specimens to investigate the damage evolution behavior of ITZs performance under the coupling actions of salt-frost cycles (SFT) and sustained compression loads. Effect of nano-silica (NS) and air-entraining agent (AE) on the saltfrost resistance strengthening for ITZs inside RAC was further explored. The apparent morphology and the relative dynamic elastic modulus (RDEM) of modified simulant multiple ITZs of RAC were measured to characterize the salt frost damage, and further the microstructural analysis including microhardness, laser scanning microscope (LSM) and SEM observation was conducted, aiming at revealing the salt-frost damage mechanisms of simulant modified ITZs inside RAC. The results indicate that the appropriate dosage of NS and AE could effectively reduce the salt-frost scaling of RAC by strengthening the internal microstructures. The RDEM of NSmodified RAC samples incorporating with AE was always higher than NS-modified RAC and non-modified RAC. After NS-modified, the minimum microhardness of old ITZs was increased by 10.2 % and the thickness was averagely reduced by about 10 mu m. The microhardness loss of modified RAC after SFT was relatively smaller. On the contrary, applying loading with higher compressive stress level markedly accelerates the salt-frost damage process of non-modified and modified ITZs. The results of SEM and LSM tests showed there is less salt-frost damage under sustained compression loads due to the denser microstructures of ITZs after synergistic modification by NS and AE. This is demonstrated by stronger bonding properties between original aggregate and old mortar and less elevation differences at old/new ITZs. Above all, this study explores the evolving trends of salt-frost damage and microstructure for simulant ITZs inside RAC under the coupling actions of sustained compression loads and SFT, which can provide some basis for the durability assessment of RAC structures exposed to cold region.

Salt frost damage evolution and transport properties of recycled aggregate concrete under sustained compressive loading

RBSM-based Mesoscale Study of Frost Deterioration for Recycled Concrete Considering Air-Entrainment in Old and New Mortar

Coupled Effects of the Freeze-Thaw Cycles and Salt Erosion on the Performance of Recycled Aggregate Concrete

Characterizations and Quantification of Freeze-Thaw Behaviors of Recycled Brick Aggregate Concrete

Improving the salt frost resistance of recycled aggregate concrete modified by air-entraining agents and nano-silica under sustained compressive loading

Salt-frost Damage Characterization of Simulant Multiple ITZs in Nano-Silica Modified Recycled Aggregate Concrete

Flexural Behavior and Durability Properties of Recycled Aggregate Concrete (RAC) Beams Subjected to Long-Term Loading and Chloride Attacks

Frost Resistance of Recycled Aggregate Concrete: A Critical Review

Salt-frost scaling resistance characteristics of nano silica-modified recycled aggregate concrete

Deterioration Performance of Recycled Aggregate Pervious Concrete under Freezing–Thawing Cycle and Chloride Environment

Frost Durability of Self-Compacting Concrete Prepared with Aeolian Sand and Recycled Coarse Aggregate

Chloride permeability of recycled aggregate concrete under the coupling effect of freezing-thawing, elevated temperature or mechanical damage

Evaluation indexes of the frost resistance of recycled aggregate concrete and improvement mechanisms: A review

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Freeze-Thaw Resistance and Microstructural Analysis of Recycled Aggregate Concrete Incorporating Ferronickel Slag As Fine Aggregate

Experimental Study and Microscopic Analysis on Frost Resistance of Iron Ore Tailings Recycled Aggregate Concrete

Freeze-thaw Resistance of Recycled Aggregate Concrete Incorporating Ferronickel Slag As Fine Aggregate

Effects of Imposed Damage on the Capillary Water Absorption of Recycled Aggregate Concrete

Performance Evolution of Recycled Aggregate Concrete under the Coupled Effect of Freeze-Thaw Cycles and Sulfate Attack

Frost resistance of fiber-reinforced self-compacting recycled concrete

Effect of Loading-Induced Damage on Chloride Ingress Behavior of Recycled Aggregate Concrete: A Comprehensive Review