Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Acid-catalysed Al2O3 Sol and Its Gel Material: Influence of HNO3 Content and Stability

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Effect of Aluminum Doping on the Performance and Microstructure of Methyl-Modified SiO2 Sol

Preparation of Al2O3dense films using sol derived from Al(NO3)3·9H2O

Preparation Of Al2o3 Dense Films Using Sol Derived From Al(No3)(3)Center Dot 9h(2)O

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Optical properties of amorphous Al2O3 thin films prepared by a sol–gel process

Reactive phase behavior of aluminum nitrate in high temperature and supercritical water

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Investigation of the Effects of Acid Content and Annealing on the Properties of Nanostructured TiO2 Sol

A New Sol-Gel Route to Prepare Dense Al2O3 Thin Films

Preparation and Crystallization of Si-Al Gel

Preparation And Characterisation Of Al2o3 Film On Hollow Glass Microspheres By The Sol-Gel Process

EFFECT OF NH4HCO3 ON PORE STRUCTURE OF ALUMINA

New sol-gel route using inorganic salt for synthesizing Al2O3 nanopowders

Al2O3 XEROGELS SYNTHESIZED BY INORGANIC SALT AND ORGANIC ALKOXIDE

Fabrication and Thermal Stability of La2O3 Doped Alumina Aerogel

Effect of Water Content on the Performance and Structure of Nanosized TiO2 Sol

Synthesis of Al2O3 nanopowders using inorganic salt and its physical chemistry

De-stabilization Mechanism and in Situ Solidification of Alumina Slurry Dispersed in Silica Sol

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite