Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

New sol-gel route using inorganic salt for synthesizing Al2O3 nanopowders

Synthesis of Al2O3 nanopowders using inorganic salt and its physical chemistry

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Sol-Gel Synthesis of Alumina Using Inorganic Salt Precursor

A new route to synthesis of γ-alumina nanorods

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Synthesis of Nanosized Pseudoboehmite and γ-Al2O3 by Control Precipitation Method

A New Sol-Gel Route to Prepare Dense Al2O3 Thin Films

Synthesis of Nanosized Pseudoboehmite and γ-Al<sub>2</sub>O<sub>3</sub> by Control Precipitation Method

Preparation of Rare Earth/Alkaline Earth Composite Silicates Nanopowder by Water-Based Sol-Gel Method

Preparation of nanosized CoAl2O4 powders by sol–gel and sol–gel-hydrothermal methods

Organic-free Synthesis of Boehmite Nanofibers by Al2(SO4)3·18H2O with High Pore Volume

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Non-hydrolytic sol-gel synthesis of Al2W3O12 nanopowders

Green synthesis of nanometer gamma-Al2O3 powders by sol-gel method

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Synthesis of Flower-Like Boehmite (Γ-Alooh) Via a One-Step Ionic Liquid-Assisted Hydrothermal Route

Green and Facile Synthesis of Cube-Like Γ-Alooh and Its Usage for Fabricating Mg Stabilized Na-β″-Al2O3 Powders

One-step preparation of high-purity boehmite by the effect of sugar alcohol in the aluminum-water reaction