Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Organic-free Synthesis of Boehmite Nanofibers by Al2(SO4)3·18H2O with High Pore Volume

Morphological Controlled Growth of Nanosized Boehmite with Enhanced Aspect Ratios in an Organic Additive-Free Cationic–Anionic Double Hydrolysis Method

Spontaneous Formation of Nano‐fibrillar Boehmite and the Enhancement Effect of Polyethylene Glycol

Hydrothermal Preparation Of Boehmite Nanorods By Selective Adsorption Of Sulfate

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

Hierarchical nanoarchitectonics of boehmite: The preparation of three-dimensional flower-like via hydrothermal method without surfactants

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Hydrothermal synthesis of microscale boehmite and gamma nanoleaves alumina

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

A new route to synthesis of γ-alumina nanorods

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Different nanostructures of boehmite fabricated by hydrothermal process: effects of pH and anions

Boehmite Nanowires Formation from Porous Anodic Alumina Membrane

Template-free Method for the Synthesis of High-Pore-volume Γ-Al2o3 Nanofibers in a Membrane Dispersion Microreactor.

Synthesis And Characterization Of Boehmite Alooh Nanotubes

Preparation of Large-Pore-Volume Gamma-Alumina Nanofibers with A Narrow Pore Size Distribution in A Membrane Dispersion Microreactor

Template-free method for the synthesis of high-pore-volume γ-Al 2 O 3 nanofibers in a membrane dispersion microreactor

Preparation of monolithic Al2O3–SiO2 aerogels with high-temperature resistance using boehmite nanorods

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

One-step preparation of high-purity boehmite by the effect of sugar alcohol in the aluminum-water reaction

Preparation of Pseudoboehmite with a Large Pore Volume and a Large Pore Size by Using a Membrane-Dispersion Microstructured Reactor Through the Reaction of CO2 and a NaAlO2 Solution