Abstract:A low temperature co-fired ceramic (LTCC) material of Li2ZnTi3O8–TiO2 (L2ZT3–TiO2) doped with BaO–B2O3–ZnO (BBZ) glass were prepared by conventional solid-state method. The effects of BBZ glass on the phase composition, microstructure, and microwave dielectric properties were investigated. The results indicated that BBZ glass as a sintering aid could effectively reduce the sintering temperature of L2ZT3–TiO2 ceramic below 950 °C. The XRD patterns indicated that L2ZT3–TiO2 ceramic consisted of Li2ZnTi3O8 and TiO2 phases. BBZ glass addition did not change the phase composition. In addition, the SEM demonstrated that BBZ glass could significantly improve the grain growth and densification. The sintering mechanism was analyzed through the wetting behavior and the activation energy (Ea). When added 2.5 wt% BBZ glass, the average activation energy reduced from 492.38 ± 139.03 to 370.69 ± 20.98 kJ/mol, which indicated that the BBZ glass not only effective lowered the sintering temperature but also promoted the sintering process. The L2ZT3–TiO2 ceramic with 2.5 wt% BBZ sintered at 925 °C for 4 h had excellent microwave dielectric properties of εr = 26.3, Q × f = 36,554 GHz and τf = − 4.16 ppm/°C. In addition, the good chemical compatibility of this material with Ag electrode could make it as a potential candidate for LTCC technology.

Low Temperature Sintering of Li2Zn3Ti4O12–xTiO2 Microwave Dielectric Ceramics Without Glass Addition

Low-temperature Firing and Microwave Properties of TiO 2 Modified Li 2 ZnTi 3 O 8 Ceramics Doped with B 2 O 3

Microwave Dielectric Properties of Low Temperature Sintered ZnWO4–TiO2 Composite Ceramics

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Low Temperature Sintering and Microwave Dielectric Properties of Li 2 O–3ZnO–5TiO 2 Ceramics Doped with V 2 O 5

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

Microwave Dielectric Properties and Low Temperature Firing of (1 − X)li2zn3ti4o12 –xli2tio3 (0.2 ≤ X ≤ 0.8) Ceramics with B2O3–CuO Addition

Structure and Microwave Dielectric Behaviour of Low-Temperature-fired Li2Zn1−xCoxTi3O8 (x = 0–0.07) Ceramics for Low Temperature Co-Fired Ceramic Applications

Microwave Dielectric Properties of TiO 2 -Added Li 2 ZnTi 3 O 8 Ceramics Doped with Li 2 O-Al 2 O 3 -B 2 O 3 Glass

Microwave Properties of Low-Fired Li2ZnTi3O8 Ceramics Doped with CuO–Bi2O3–V2O5

Low Temperature Sintering of Li 2 (mg 0.3 Zn 0.7 )ti 3 O 8 -0.12Tio 2 Microwave Dielectric Ceramics with Controllable Grain Size

Silver Co‐Firable Li2ZnTi3O8 Microwave Dielectric Ceramics with LZB Glass Additive and TiO2 Dopant

Research on Low Temperature Sintering of ZnO-TiO_2 Ceramics Doped with Li_2CO_3-B_2O_3-V_2O_5

Dielectric Properties and Microstructure of TiO2 Modified (znmg)tio3 Microwave Ceramics with CaO–B2O3–SiO2

Low-temperature Sintering and Microwave Dielectric Properties of ZnTiO3-based LTCC Materials

Low Temperature Sintering and Microwave Dielectric Properties of Li2ZnTi3O8–TiO2 Ceramics Doped with BaO–B2O3–ZnO Glass

Silver Co-Firable Zntinb2o8 Microwave Dielectric Ceramics With Li2o-Zno-B2o3 Glass Additive

Microwave dielectric properties of Li 2ZnTi 3O 8 ceramics doped with ZnO-B 2O 3 frit

Low Temperature Sintering Of Low-Loss Zntio3 Microwave Dielectric Ceramics With Zn-B-Si Glass

Effect of B2O3 on the Sintering and Microwave Dielectric Properties of M-phase LiNb0.6Ti0.5O3 Ceramics

Low-temperature sintering and phase component modulation of 0.95MgTiO3–0.05CaTiO3 microwave dielectric ceramics