Enhanced H2 Production from Municipal Solid Waste Gasification Using Ni–CaO–TiO2 Bifunctional Catalyst Prepared by Dc Arc Plasma Melting

Muhammad Irfan,Aimin Li,Lei Zhang,Muhammad Javid,Mengya Wang,Shujauddin Khushk

DOI: https://doi.org/10.1021/acs.iecr.9b01999

2019-01-01

Industrial & Engineering Chemistry Research

Abstract:The gasification of municipal solid waste (MSW) in the presence of a Ni-CaO catalyst is a promising approach for in situ CO2 capture along with enhanced H-2 syngas production. However, the instability of the catalyst-sorbent matrix is a challenging obstacle for the gasification process. The direct current (dc) arc plasma melting method was employed to prepare a series of bifunctional catalysts (Ni-CaO) with varied Ni loadings, while TiO2 as polymorphic transition material was added to promote the stability of the catalyst. The catalyst samples were evaluated for cyclic CO2 capture and catalytic gasification of MSW using thermogravimetric analysis (TGA) and a fixed-bed reactor, respectively. The obtained results showed that the addition of TiO2 into Ni-CaO catalyst-sorbent led to improvements in the stability of catalyst for CO2 capture. The gasification performance of a bifunctional Ni-CaO-TiO2 catalyst was evaluated on the basis of Ni loading, the catalyst to MSW (C/M) ratio, temperature, and steam rate. The results indicated that, after the addition of a Ni-CaO-TiO2 catalyst (20% Ni loading), the dry gas yield (DGY) increased from 0.75 to 1.74 Nm(3)/kg and H-2 concentration increased from 35.1 to 57.7%. Meanwhile, the tar content decreased from 9.38 to 2.55% with the addition of the catalyst. The significant influences of Ni loading, C/M ratio, gasification temperature, and steam on product composition and characteristics were also evaluated. Tar analysis indicated that steam and catalyst addition resulted in tar reduction, which led to a higher DGY. Moreover, an unconventional method (i.e., thermal plasma technique) was employed for the catalyst preparation, which demonstrated promising results for MSW gasification with an industrial application prospect.