Abstract:The durability of mortar in actual environment is a basic research subject in the current concrete engineering field, and the research on freezing-thawing characteristics of mortar has become one of its important topics. In this paper, physical-mechanical proprieties and freezing-thawing damage mechanisms of mortar samples were carried out under frost action. Meanwhile, ions concentrations (Ca2+ and Mg2+) dissolved in sodium sulfate solutions were also monitored during the freezing-thawing cycle. The test results showed that physical-mechanical proprieties of mortar samples had a significant trend of gradual deterioration under the action of chemical solutions. Compared with sound mortar, cohesion for mortar samples after 60 freeze-thawing cycles decreased by 37.1%, 26.8%, and 20.9%, when samples soaked in pH=3.0 of Na2SO4, pH=12.0 of NaOH, and pH=7.0 of Na2SO4 solutions, respectively, and internal friction angle decreased by 18.4%, 14.2%, and 7.3%, respectively. This indicated that the degree of damage to the cohesion of samples was greater than that of the internal friction angle. Uniaxial compressive strength of mortar samples has a linear relationship with the damage variable, and peak axial strain has an exponential relationship with the damage variable. Meanwhile, the degree of freezing-thawing deterioration was quantitatively analyzed based on changes in porosity of the samples. There were obvious relationships between ions concentrations and physical-mechanical proprieties. And the correlations relationships among the damage variables, physical-mechanical proprieties of mortar, and Ca2+ and Mg2+ ion concentrations are indirectly obtained, that is, the degradation law of physical-mechanical proprieties of mortar is influenced by damage variables and Ca2+ and Mg2+ ion concentrations.

Coupled effect of relative humidity and temperature on the degradation of cement mortars partially exposed to sulfate attack

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Coupling Effect of Temperature and Relative Humidity Diffusion in Concrete under Ambient Conditions

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Chloride Diffusivity Change of Inadequate Cured Mortar Subjected to Sulphate Attack Using Mini-Migration Method

Effects of Temperature and Moisture on Concrete-PCM Interface Performance

Erosion of Aerial Lime and Sticky Rice Mortars by Cyclic Wetting–drying and Dilute Sulfate Acid Actions

Effect of Sulphur-Containing Tailings Content and Curing Temperature on the Properties of M32.5 Cement Mortar

A chemo-thermo-damage-transport model for concrete subjected to combined chloride-sulfate attack considering the effect of calcium leaching

Effect of Moisture Content and Porosity on Compressive Strength of Concrete During Drying at 105 °C

Quantifying Isothermal Drying of Cement Mortars in View of Water Sensitivity

Effect of Hydration Temperature Rise Inhibitor on the Temperature Rise of Concrete and Its Mechanism

Influences of water by cement ratio on mechanical properties of mortars submitted to drying

Influence of moisture condition on chloride diffusion in partially saturated ordinary Portland cement mortar

Mechanical characteristics and freezing-thawing degradation mechanism for mortar samples under sodium sulfate solutions attack

Effect of Temperature on Pore Structure and Strength of Concrete

Microstructure-Based Relative Humidity in Cementitious System Due to Self-Desiccation

Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles

Effect of Elevated Temperatures on Compressive Strength of Concrete