Abstract:The construction of deeply buried tunnels has intensified concerns regarding shrinkage cracking and the long-term performance deterioration of lining concrete in dry-hot environments. These issues are related to the dynamic interconversion of internal moisture states, the changing moisture behavior over time, and the evolution of calcium silicate hydrate (C-S-H) properties. However, the mechanisms underlying these phenomena are not fully understood. This study investigates the dynamics of moisture content across different states, the source and composition of evaporated water, as well as the mechanism of change in the microscopic properties of C-S-H in concrete subjected to dry-hot conditions (40°C and 60°C) and standard curing environments through tests on water loss rates, chemically bound water, and low-field nuclear magnetic resonance. The findings reveal that at 40°C and 60°C, hydration products were generated rapidly before mold removal, leading to significant increases in chemically bound water, interlayer water, and gel water, while capillary water was notably consumed. After mold removal, the rate of chemically bound water increase slowed, while interlayer water, gel water, and capillary water evaporated significantly, with gel water comprising 87.27 % and 83.51 % of the evaporated water at 40°C and 60°C, respectively. From day 1 to day 28, interlayer water, gel water, and capillary water contents decreased significantly, with reductions of up to 85.98 % at 60°C. In dry-hot environments, moisture primarily exists as chemically bound water and gel water, contrasting with standard curing conditions where capillary water is also present. The study concludes that drying of C-S-H gels leads to both positive effects, such as interlayer space compression and increased indentation modulus, and negative effects, including increased microporosity and reduced matric densification, ultimately contributing to the deterioration of long-term mechanical properties.

Effect of Moisture Content and Porosity on Compressive Strength of Concrete During Drying at 105 °C

Effect of Elevated Temperatures on Compressive Strength of Concrete

Effect of Temperature on Pore Structure and Strength of Concrete

Effect of Different Humidity-Controlling Modes on Microstructure and Compressive Behavior of Ordinary Concrete

Transport properties of concrete after drying-wetting regimes to elucidate the effects of moisture content, hysteresis and microcracking

Effects of Temperature and Moisture on Concrete-PCM Interface Performance

Moisture Diffusion Coefficient of Concrete under Different Conditions

Time-varying moisture characteristics and C-S-H gel properties of concrete in dry and hot environments

Effects of Moisture on Properties of Concrete Exposed to Elevated Temperature

Coupling Effect of Temperature and Relative Humidity Diffusion in Concrete under Ambient Conditions

A Coupled Hygro-Thermal Model of Early-Age Concrete Based on Micro-Pore Structure Evolution

Influences of water by cement ratio on mechanical properties of mortars submitted to drying

Experimental Study of Thermal-Hydraulic-Mechanical Coupling Behavior of High-Performance Concrete

Variation Pattern of the Elastic Modulus of Concrete under Combined Humidity and Heat Conditions

Effect of Cementitious Permanent Formwork on Moisture Field of Internal-Cured Concrete under Drying

Effect of Curing Temperature on Mechanical Strength and Thermal Properties of Hydraulic Limestone Powder Concrete

Experimental Study on the Internal Relative Humidity in Concrete under Dry-Wet Cycles

Characterization of Thermal Damage and Compressive Strength During Drying at Elevated Temperatures Using Ultrasonic Pulse Velocity

Effect of thermal fatigue on mechanical properties and microstructure of concrete in constant ambient humidity

Effect of steam curing regimes on temperature and humidity gradient, permeability and microstructure of concrete

Effect of Pore Liquid Viscosity on the Dynamic Compressive Properties of Concrete