Abstract:The loss of strength and durability caused by early frost attack is the macro performance of internal microstructure deterioration. Understanding the influence mechanism of early frost attack at the micro level is necessary to avoid or minimize the early frost attack to macro performance. In this study, the influence of early frost attack on the strength, water sorptivity, chloride permeability, and microstructure of cement mortar was investigated. The fresh mortars were pre-cured for 10, 12, 14, and 16 h and then frozen at -10 degrees C for 7 days to simulate an early frost attack. After freezing, the standard curing (20 degrees C) was carried out until the testing. It is found that after standard curing of 28 days, the strength of early-frozen mortar can reach more than 95 % of the 28-day strength of unfrozen mortar. Interestingly, the sorptivity coefficient and total charge passed of earlyfrozen mortar are much higher than the level of unfrozen mortar, and the loss of resistance to water penetration and chloride ion penetration exceeds 20 %, indicating that early frost attack causes more severe damage to the durability than to the strength of mortar. Mercury intrusion porosimetry (MIP) results show that early frost attack can increase the pore volume of >50 nm and coarsen the pores within 10-50 nm. Correspondingly, key pore parameters (critical pore diameter, threshold pore diameter, and tortuosity) that affect the durability of mortar are also negatively affected. Energy dispersive spectroscopy (EDS) analysis also shows that after suffering early frost attack, the interfacial transition zone (ITZ) thickness of mortar is increased from 4 to 10 mu m to 8-13 mu m, and the probability of high Ca/Si ratios (4-10) in the ITZ is also increased. Finally, it is concluded that the coupling effect of pore structure coarsening and ITZ degradation leads to more severe durability loss.

Chloride Diffusivity Change of Inadequate Cured Mortar Subjected to Sulphate Attack Using Mini-Migration Method

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Prediction of Effective Chloride Diffusivity of Cement Paste and Mortar from Microstructural Features

Influence of Initial Curing Conditions and Exposure Environments on Chloride Migration in Concrete Using Electrochemical Method

Change of the Coefficient of Thermal Expansion of Mortar Due to Damage by Freeze Thaw Cycles

Influence of moisture condition on chloride diffusion in partially saturated ordinary Portland cement mortar

Electrical Response of Mortar Saturated with NaCl Solutions under Freeze–Thaw Cycles

EXPERIMENTAL STUDY ON THE CHLORIDE DIFFUSION OF CONCRETE BASED ON ITS PORE STRUCTURE

Diffusion Characteristic of Sulfate Anion in Surface Region of Cement Mortar at Early Stage

Mechanical characteristics and freezing-thawing degradation mechanism for mortar samples under sodium sulfate solutions attack

Effect of Electric Field on the Degradation Process of Reinforced Mortar under Chloride and Sulfate Attack

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Effect of Exposure Conditions on Mortar Subjected to an External Sulfate Attack

Chloride Binding Capacity and Its Effect on the Microstructure of Mortar Made with Marine Sand

Study on the Influence of Early Frost Attack on the Performance of Cement Mortar

A chemo-thermo-damage-transport model for concrete subjected to combined chloride-sulfate attack considering the effect of calcium leaching

Evaluating the chloride diffusion coefficient of cement mortars based on the tortuosity of pore structurally-designed cement pastes