Abstract:The deterioration issues of surface strength reduction occur in cemented soil exposed to marine corrosion environment for long-term, which seriously affects the durability and safety of the structure. Therefore, it is urgent to reveal the tempo-spatial deterioration mechanisms of cemented soil, which can provide a theoretical basis for practical anti-deterioration measures. In this study, the micro-cone penetration test of cemented soil exposed to seawater was conducted, and the ion profiles, pH, X-ray diffraction (XRD), and scanning electron microscopy with energy disperse spectroscopy (SEM–EDS) tests of different slice layers from the exposed surface were performed. The results show that the deteriorated cemented soil along the erosion direction can be classified into completely deteriorated layer with zero-strength, deteriorated transition layer with only about 10% strength remaining, and an undeteriorated zone with no strength reduction. The depth of the deteriorated zone increased with corrosion time and decreased with cement content, but the strength reduction was not affected. The micro-cone penetration, ion concentration, pH, XRD and SEM–EDS results illustrated that the essential nature of deterioration of cemented soils is the tempo-spatial evolution of corrosive ions enriched by corrosion reactions and gradually induced the phase change of hydration products into non-cementitious or secondary expansion products, which ultimately leads to the strength reduction in surface layers. Moreover, Mg 2+ and SO 4 2− were mainly enriched in the deteriorated zone, and Cl − could invade and enrich in the undeteriorated zone. Besides, the leaching of Ca 2+ and OH − was associated with the invasion of all these corrosive ions. This study contributes to the deterioration mechanism of cemented soil and provides useful reference for the development of seawater anti-corrosion binder.

Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Influence of Sulfate on the Chloride Diffusion Mechanism in Mortar

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Degradation Progress and Protection of Cement Mortars Partially Immersed in Sulfate–chloride Solution

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

Degradation of Mortar Fully Buried in Saline Soil Containing Sodium Sulfate or Magnesium Sulfate

Study on Concrete Deterioration and Chloride Ion Diffusion Mechanism by Different Aqueous NaCl-MgSO4 Concentrations

A chemo-thermo-damage-transport model for concrete subjected to combined chloride-sulfate attack considering the effect of calcium leaching

Deterioration Mechanism of Plain and Blended Cement Mortars Partially Exposed to Sulfate Attack

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

The Deterioration of Cement Mortar under the Coupled Conditions of Stray Current and Sulfate

Influence of Ca2+ on Early Degradation of Cast-In-Situ Mortar Induced by Sulfate-Magnesium Multiple Combined Attack

Deteriorated characteristics, elemental zonation, and phase changes in the surface of cemented soil exposed to marine environment

Effect of Multiple Ions on the Degradation in Concrete Subjected to Sulfate Attack

Study on the Deterioration Process of Cement‐based Materials under Sulfate Attack and Drying–wetting Cycles

The Influence of Multiple Combined Chemical Attack on Cast-in-situ Concrete: Deformation, Mechanical Development and Mechanisms

Effect of Chlorine Salt on Durability of Mineral Admixture Concrete under Different Conditions