Abstract:Urban underground engineering is generally buried at a shallow depth and suffers long-term environmental water effects such as rainfall, rivers, underground pipeline leakage, and groundwater. The mechanical properties of the structures are affected by constant deterioration, which seriously hinders the safe, healthy, and sustainable development of the city. On the basis of on-site investigation of civil defense engineering, this article simulates the water environment conditions of mortar in underground engineering in the laboratory and conducts manual sample preparation in the laboratory. Then, water, H2CO3, NaCl, and Na2CO3 solution or wet–dry cycles are used to corrode the sample, respectively. A uniaxial compression test, Brazilian splitting test, analyses of the acoustic emission signals and electromagnetic signals, and magnetic imaging testing are performed, respectively. The results show that an increase in the action time of environmental water leads to a gradual increase in the uniaxial compressive strength, tensile strength, and elastic modulus of cement mortar, but it will decrease over a long period of time. Different environmental water components can also lead to a different performance of soaked mortar. The uniaxial compressive strength R, tensile strength σt, and elastic modulus E of mortar samples exhibit values in different solutions in the order of H2CO3 solution<NaCl solution<Na2CO3 solution<water. A moderate solution soak time can enhance the mechanical properties of the mortar, but this effect decreases at long time scales. The effect of wet–dry cycles on the mechanical properties and degradation process of mortar is significant. With the increase in wet–dry cycles, the porosity of mortar continuously increases. The cumulative ringing count, energy, amplitude, and impact number of acoustic emission signals always increase when the samples are loaded to failure. The uniaxial compressive strength, tensile strength, and elastic modulus first increase and then decrease. The experimental results lay the foundation for further investigating the performance changes in mortar under complex water environments in underground engineering.

Mechanical characteristics and freezing-thawing degradation mechanism for mortar samples under sodium sulfate solutions attack

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Electrical Response of Mortar Saturated with NaCl Solutions under Freeze–Thaw Cycles

Compositional Dependence of Pore Structure, Strengthand Freezing-Thawing Resistance of Metakaolin-Based Geopolymers

Estimation of Ice Formation in Mortar Saturated with Sodium Chloride Solutions

Change of the Coefficient of Thermal Expansion of Mortar Due to Damage by Freeze Thaw Cycles

DETERIORATION CHARACTERISTICS OF CEMENT MORTAR BY PHYSICAL ATTACK OF SODIUM SULFATE

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Study on the Influence of Early Frost Attack on the Performance of Cement Mortar

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

Degradation of Mortar Fully Buried in Saline Soil Containing Sodium Sulfate or Magnesium Sulfate

Coupling effect of salt freeze-thaw cycles and cyclic loading on performance degradation of carbon nanofiber mortar

Study on the Deterioration Process of Cement‐based Materials under Sulfate Attack and Drying–wetting Cycles

Experimental Study on the Effect of Environmental Water on the Mechanical Properties and Deterioration Process of Underground Engineering Masonry Mortar

Influence of Synthetic Limestone Sand on the Frost Resistance of Magnesium Potassium Phosphate Cement Mortar

Research on the Mechanical Properties and NMR Characteristics of Cement Mortar during Freeze-Thaw Cycles

Analysis of freeze-thaw damage and pore structure deterioration of mortar by low-field NMR

Deterioration Mechanism of Plain and Blended Cement Mortars Partially Exposed to Sulfate Attack

The Mechanical Properties of Mortar Blended with Steel-PVA Hybrid Fibers and CaCO 3 Whiskers under Freeze/Thaw Cycles Condition

Deterioration behaviors of sulfate crystallization attack on cement-based material